Several studies have addressed the use of antibacterial coating to reduce implant-associated infections. In this study, novel silver (Ag)-containing calcium-phosphate (CP) coating technology based on the thermal spraying method was developed. The coating's physical and chemical properties, in vitro antibacterial activity, hydroxyapatite (HA)-forming ability, and release of Ag ions were evaluated. An amorphous structure of the coating was confirmed by X-ray diffraction, and Ag residue in the coating was determined by elementary analysis. The coating showed strong antibacterial activity to methicillin-resistant Staphylococcus aureus in fetal bovine serum (FBS) along with HA-forming ability in simulated body fluid. Therefore, it is expected that the coating would confer antibacterial and bone bonding abilities to the implant surface. Time course release testing of Ag ions from the coating on immersion in FBS showed pronounced Ag release for up to 24 h after immersion, with consistent strong antibacterial activity at the early postoperative stage. In repeated testing, the amount of released Ag ions was about 6500 parts per billion (ppb, microg/L) for the first release test, after which it gradually decreased. However, retention of significant release of Ag ions after a sixth repeat implies that Ag release from the coating is slow in FBS.

No abstract

Bacterial infection is a serious postoperative complication of joint replacement. To prevent infections related to implantation, we have developed a novel antibacterial coating with Ag-containing hydroxyapatite (Ag-HA). In the present study, we examined the antibacterial activity of Ag-HA implant coatings in the medullary cavity of rat tibiae. Forty 10-week-old rats received implantation of Ag-HA-or HA-coated titanium rods, then were inoculated with $1.0 Â 10 2 colony-forming units of methicillin-resistant Staphylococcus aureus. Bacterial counts were calculated for rats euthanized at 24, 48, and 72 h postoperatively. Serum levels of Ag (in the Ag-HA group only) were calculated for rats euthanized at 24, 48, 72 h and 4 weeks. Radiographic evaluations of bone infection were also performed at 4 weeks. Tibiae from both groups showing infection were evaluated histologically. Significant differences in bacterial counts were seen at 24, 48, and 72 h. Mean concentrations of Ag in serum peaked about 48 h after implantation, then gradually decreased. Mean radiographic scores for infection were significantly lower with Ag-HA implants than with HA implants. Histological examination showed better results for abscesses, bone resorption, and destruction of cortical bone around Ag-HA-coated implants. These results indicate that Ag-HA coatings may help prevent surgical-site infections associated with joint replacement. ß

One of the serious postoperative complications associated with joint replacement is bacterial infection. In addressing this problem, we have previously described the development of a novel thermal spraying technology combining silver (Ag) showing antibacterial activity with hydroxyapatite (HA) displaying good biocompatibility and osteoconductivity, and reported the in vitro properties. This study evaluated serum Ag ion concentrations and antibacterial activity against methicillin-resistant Staphylococcus aureus (MRSA) using a subcutaneous rat model. HA loaded with 3 wt % of silver oxide (Ag-HA) and plain HA were sprayed on the surface of titanium disks. Ag-HA- or HA-coated samples were implanted into the back subcutaneous pockets of male Sprague-Dawley rats. Mean serum Ag ion concentration in the Ag-HA group increased to more than 50 ppb by 48 h after implantation, then decreased gradually to baseline levels. Mean (+/- standard error of the mean) number of viable MRSA on HA coating was (1.5 +/- 0.5) x 10(5), which is significantly more than the (1.1 +/- 0.4) x 10(4) on Ag-HA coating (p < 0.001). Ag-HA coating offers good abilities to release Ag ions and kill MRSA in vivo.

No abstract