Polyimide gels are produced by cross-linking anhydride capped polyamic acid oligomers with aromatic triamine in solution and chemically imidizing. The gels are then supercritically dried to form nanoporous polyimide aerogels with densities as low as 0.14 g/cm(3) and surface areas as high as 512 m(2)/g. To understand the effect of the polyimide backbone on properties, aerogels from several combinations of diamine and dianhydride, and formulated oligomer chain length are examined. Formulations made from 2,2'-dimethylbenzidine as the diamine shrink the least but have among the highest compressive modulus. Formulations made using 4,4'-oxydianiline or 2,2'dimethylbenzidine can be fabricated into continuous thin films using a roll to roll casting process. The films are flexible enough to be rolled or folded back on themselves and recover completely without cracking or flaking, and have tensile strengths of 4-9 MPa. Finally, the highest onset of decomposition (above 600 °C) of the polyimide aerogels was obtained using p-phenylene diamine as the backbone diamine with either dianhydride studied. All of the aerogels are suitable candidates for high-temperature insulation with glass transition temperatures ranging from 270-340 °C and onsets of decomposition from 460-610 °C.
Silica aerogels are highly porous solid materials consisting of three-dimensional networks of silica particles and are typically obtained by removing the liquid in silica gels under supercritical conditions. Several unique attributes such as extremely low thermal conductivity and low density make silica aerogels excellent candidates in the quest for thermal insulation materials used in space missions. However, native silica aerogels are fragile at relatively low stresses. More durable aerogels with higher strength and stiffness are obtained by proper selection of silane precursors and by reinforcement with polymers. This paper first presents a brief review of the literature on methods of silica aerogel reinforcement and then discusses our recent activities in improving not only the strength but also the elastic response of polymer-reinforced silica aerogels. Several alkyl-linked bis-silanes were used in promoting flexibility of the silica networks in conjunction with polymer reinforcement by epoxy.
The mesoporous surfaces of TMOS-derived silica aerogels have been modified with amines by copolymerization of TMOS with APTES. The amine sites have become anchors for cross-linking the nanoparticles of the skeletal backbone of the aerogel by attachment of di-, tri-, and tetra-functional epoxies. The resulting conformal coatings increase the density of the native aerogels by a factor of 2−3 but the strength of the resulting materials may increase by more than 2 orders of magnitude. Processing variables such as the amount of APTES used to make the gels, the epoxy type and concentration used for cross-linking, and the cross-linking temperature and time were varied according to a multivariable design-of-experiments (DOE) model. It was found that while elastic modulus follows a similar trend with density, maximum strength is attained neither at the maximum density nor at the highest concentration of −NH2 groups, suggesting surface saturation effects. Aerogels cross-linked with the trifunctional epoxide always show improved strength compared with aerogels cross-linked with the other two epoxides under identical conditions. Solid 13C NMR studies show residual unreacted epoxides, which condense with one another by heating cross-linked aerogels at 150 °C.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.