Hydrothermal synthesis of CeO2was optimized on two reactant concentrations and synthesis temperature and duration, in order to achieve material having the greatest specific surface area (SSA). Taguchi method of experimental design was employed in evaluation of the relative importance of synthesis parameters. CeO2nanoparticles were characterized using X-ray diffraction, nitrogen adsorption-desorption isotherms, and scanning electron microscopy. Optimum conditions for obtaining particles with greater SSA were calculated according to Taguchi’s model “the-higher-the-better.” Synthesis temperature was found to be the only parameter significant for enabling nanoparticles with greater SSA. Mesoporous nanocrystalline ceria with SSA as great as 226 m2 g−1was achieved, which is unprecedented for the hydrothermally synthesized ceria. The reason for this achievement was found in temperature dependence of the diffusion coefficient which, when low, favors nucleation yielding with fine particles, while when high it favors crystal growth and formation of one-dimensional structures. The occurrence of 1D-structure in sample exhibiting the smallest SSA was confirmed. Very fine crystallites with crystallite size as low as 5.9 nm have been obtained being roughly inverse proportional to SSA. Selected samples were tested as catalyst for soot oxidation. Catalyst morphology turned out to be decisive factor for catalytic activity.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.