Carbon fiber is a material with a vast area of utilization. When combined with a resin, we get a composite, which provides great mechanical properties, has low mass and can be utilized in many different applications. Carbon fiber cloth can be found in a wide range of forms and shapes, differing from weight to the shape of their weave. Manufacturing a composite part can be achieved with a variety of techniques and processes, each of them having advantages and disadvantages over the other. One of the most common process for producing composite parts is the open moulded hand lay-up process. This process is economically viable, has low cost for equipment, and can produce parts with satisfactory results. A composite sheet is manufactured using the hand lay-up process. Three testing samples are taken out from the composite sheet, and their tensile strength is determined using the ASTM D3039 standard.
The ternary copper antimony oxide Cu3‐xSb1+xO5.5+3x/2 (x=0.23) has been synthesized under 0.8–1.3 MPa pO2 at 1022–1082 °C. Rietveld refinements of X‐ray and neutron powder diffraction patterns concluded that the oxide adopts a bixbyite type structure, crystallising in the cubic space group Ia‐3 with the unit cell parameter a=9.61164(4) Å at room temperature from powder neutron diffraction data. The cationic 8b and 24d sites were found to be occupationally disordered where both Cu and Sb could be found on both sites. This is supported by X‐ray absorption spectroscopy experiments showing more than one possible Cu environment. There was a significant net deficiency of oxygen in the compound which was first inferred from observations of a thermochromic‐like phenomena and also seen from in situ high temperature neutron diffraction experiments. Magnetic susceptibility and magnetization measurements show paramagnetic behaviour with spin‐glass like transition below 6 K.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.