We report on photodarkening (PD) investigations at Yb doped fibers with specific variation of the concentrations of the codopants aluminum and phosphorus, measured during cladding pumping at 915 nm. A core composition with equal content of Al and P is most promising to achieve Yb fibers with low PD, high laser efficiency and low numerical aperture of the laser core despite of high codoping. A laser output power of more than 100 W was demonstrated on such a fiber with a slope efficiency of 72%. The correlation of the PD loss with the NIR-excited cooperative luminescence encourages the supposition that cooperative energy transfer from excited Yb(3+) ions to the atomic defect precursors in the core glass enables the formation of color centers in the pump-induced PD process.
We report on the characteristics of an active fiber with core material made by sintering of Yb-doped silica powders as an alternative to a conventional modified chemical vapor deposition (MCVD) technique. This material provides the possibility to design very large and homogenously rare-earth doped active fiber cores. We have determined a fiber background attenuation of 20 dB/km and measured a slope efficiency of 80%. These values are comparable to established fibers made by MCVD technology.
We report on the thermal treatment of photodarkened Yb-doped fiber samples. The method of non-isothermal bleaching at different temperature ramp rates can be used to determine the thermal energy distribution of photodarkening induced color centers. A distributed activation energy with a mean value of about 1.3 eV and a FWHM of 0.5 eV was found. Spectral changes during thermal treatment were observed and could be interpreted, e.g. as an enhancement of the absorption cross section.
We report on detailed investigations of ytterbium (Yb) and aluminum (Al) doped silica fiber and preform samples co-doped with cerium (Ce). The prevention of pump-induced photodarkening (PD) by temporary oxidation of Ce3+ to Ce4+ (or rather Ce3++) was proved by observed modifications in the ultraviolet (UV) spectra of transient absorption during near-infrared (NIR) pumping of thin preform slices. Only a small part of available Ce3+ ions (< 4%) was found to be involved in this process despite Yb inversions of up to 0.28. The modifications in the UV absorption spectra disappeared completely when the pump power was switched-off. From these observations we conclude that the recombination to Ce3+ takes place very fast thereby enabling these ions to capture liberated holes h+ perpetually during further pumping. We found a concentration ratio of Ce/Yb ≈0.5 to be sufficient to reduce PD loss to 10% in comparison to Ce-free fibers. Thus, the thermal load caused by absorption of PD color centers at pump (and laser) wavelength is expected to be also reduced. Unfortunately, new heat sources arise with the presence of Ce which cannot be explained by the absorption of Ce ions at the pump wavelength but must be attributed to the interaction with excited Yb ions. Fiber temperature increase of more than 200 K was observed if both, Yb2O3 and Ce2O3 concentration exceed 0.4 mol%.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.