The syntheses and comprehensive characterization of 14 organic semiconductors based on perylene bisimide (PBI) dyes that are equipped with up to four halogen substituents in the bay area of the perylene core and five different highly fluorinated imide substituents are described. The influence of the substituents on the LUMO level and the solid state packing of PBIs was examined by cyclic voltammetry and single crystal structure analyses of seven PBI derivatives, respectively. Top-contact/bottom-gate organic thin film transistor (OTFT) devices were constructed by vacuum deposition of these PBIs on SiO(2) gate dielectrics that had been pretreated with n-octadecyl triethoxysilane in vapor phase (OTS-V) or solution phase (OTS-S). The electrical characterization of all devices was accomplished in a nitrogen atmosphere as well as in air, and the structural features of thin films were explored by grazing incidence X-ray diffraction (GIXD) and atomic force microscopy (AFM). Several of those PBIs that bear only hydrogen or up to two fluorine substitutents at the concomitantly flat PBI core afforded excellent n-channel transistors, in particular, on OTS-S substrate and even in air (mu > 0.5 cm(2) V(-1) s(-1); I(on)/I(off) > 10(6)). The best OTFTs were obtained for 2,2,3,3,4,4,4-heptafluorobutyl-substituted PBI 1a ("PTCDI-C4F7") on OTS-S with n-channel field effect mobilities consistently >1 cm(2) V(-1) s(-1) and on-to-off current rations of 10(6) in a nitrogen atmosphere and in air. For distorted core-tetrahalogenated (fluorine, chlorine, or bromine) PBIs, less advantageous solid state packing properties were found and high performance OTFTs were obtained from only one tetrachlorinated derivative (2d on OTS-S). The excellent on-to-off current modulation combined with high mobility in air makes these PBIs suitable for a wide range of practical applications.
Core‐chlorinated naphthalene tetracarboxylic diimides (NDIs) with fluoroalkyl chains are synthesized and employed for n‐channel organic thin‐film transistors (OTFTs). Structural analyses of the single crystals and thin films are performed and their charge‐transport behavior is investigated in terms of structure–property relationships. NDIs with two chlorine substituents are shown to exhibit a herringbone structure with a very close π‐plane distance (3.3–3.4 Å), a large π‐stack overlap (slipping angle ca. 62°), and high crystal densities (2.046–2.091 g cm−3). These features result in excellent field‐effect mobilities of up to 1.43 cm2 V−1 s−1 with minimal hysteresis and high on–off ratios (ca. 107) in air. This is similar to the highest n‐channel mobilities in air reported so far. Despite the repulsive interactions of bulky Cl substituents, tetrachlorinated NDIs adopt a slip‐stacked face‐to‐face packing with an interplanar distance of around 3.4 Å, resulting in a high mobility (up to 0.44 cm2 V−1 s−1). The air‐stability of dichlorinated NDIs is superior to that of tetrachlorinated NDIs, despite of their higher LUMO levels. This is closely related to the denser packing of the fluorocarbon chains of dichlorinated NDIs, which serves as a kinetic barrier to the diffusion of ambient oxidants. Interestingly, these NDIs show an optimal performance either on bare SiO2 or on octadecyltrimethoxysilane (OTS)‐treated SiO2, depending on the carbon number of the fluoroalkyl chains. Their synthetic simplicity and processing versatility combined with their high performance make these semiconductors highly promising for practical applications in flexible electronics.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.