Glass (GFR) and carbon fiber-reinforced (CFR) dual-cure polymer composites fabricated by UV-assisted three-dimensional (UV-3D) printing are presented. The resin material combines an acrylic-based photocurable resin with a low temperature (140 °C) thermally-curable resin system based on bisphenol A diglycidyl ether as base component, an aliphatic anhydride (hexahydro-4-methylphthalic anhydride) as hardener and (2,4,6,-tris(dimethylaminomethyl)phenol) as catalyst. A thorough rheological characterization of these formulations allowed us to define their 3D printability window. UV-3D printed macrostructures were successfully demonstrated, giving a clear indication of their potential use in real-life structural applications. Differential scanning calorimetry and dynamic mechanical analysis highlighted the good thermal stability and mechanical properties of the printed parts. In addition, uniaxial tensile tests were used to assess the fiber reinforcing effect on the UV-3D printed objects. Finally, an initial study was conducted on the use of a sizing treatment on carbon fibers to improve the fiber/matrix interfacial adhesion, giving preliminary indications on the potential of this approach to improve the mechanical properties of the 3D printed CFR components.
In this work, a newly prepared cationic/free-radical photopolymer, which consists of two epoxies and a tetrafunctional acrylate, is presented for the first time for a visible light stereolithography (SL), showing the advantages of both cationic and free-radical resins. An onium salt, commonly used as a cationic UV initiator, and a photosensitizer make the blend suitable for a near-visible (405 nm) SL. An increase in the polymerization rate and a drop in the induction period are observed for the newly prepared cationic/free-radical blend, compared with either only cationic systems or free-radical resins. This suggests that the combination of cationic and free-radical polymerizations in a single resin has a positive synergistic effect. The addition of silica nanoparticles to the blend provides a reinforcing and toughening effect. Indeed, the resin loaded with silica shows a 31% increase in the elastic modulus, compared with the unfilled resin. Regarding the values of tensile strength and elongation at break, they, respectively, grow by 47 and 15%, when the nanocomposite resin is compared with the neat resin. A very low volumetric shrinkage of 0.7% and a remarkable printing quality of objects obtained with this new photopolymer will enable the 3D printing of microrobots, bioengineering microdevices, and sensors.A key characteristic of onium salts is the possibility of undergoing either homo-or heterolytic cleavage, simultaneously producing either a radical cation/aryl radical pair or an aryl cation. 22,23 Therefore, the same photoinitiator may start both cationic and Additional Supporting Information may be found in the online version of this article. M. Invernizzi and R. Suriano contributed equally to this article.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.