Polypropylene (PP) is a promising material for extrusion-based additive manufacturing due to its low cost, chemical resistance, good mechanical properties, versatile, and can be applied in various industrial applications. Recent research has focused on addressing the warpage issue in 3D printing of PP filaments. The effect of environmental conditions and loading of nanoprecipitated calcium carbonate (NPCC) in the pristine polypropylene to decrease warpage using the Fused Deposition Modelling (FDM) printing technology was studied. PP-NPCC composite filaments containing 5, 10, and 15 NPCC (wt%) were prepared using the twin-screw extruder. The printability, physicochemical, and mechanical properties of the PP-NPCC blends were determined. Based on the results, the incorporation of NPCC has contributed to the improvement of 3D printability and warpage in the PP-NPCC composite. At controlled environmental conditions, the filament was printable and the warpage was decreased by 44% at 10% NPCC loading. At the same concentration, there was a 30% increase in compressive strength and 43% increase in elastic modulus of the 3D printed parts.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.