A new strategy to achieve easily scalable triple stimuli-responsive elastomeric opal films for applications as stretch-tunable photonic band gap materials is reported. Novel monodisperse highly functional core-interlayer-shell beads are obtained by semicontinuous emulsion polymerization featuring a temperature-sensitive fluorescent rhodamine dye either locally restricted in the core or the shell of prepared beads. After extrusion and compression molding, homogeneous elastomeric opal films with fascinating stretch-tunable and temperature-dependent fluorescent properties can be obtained. Applying strains of only a few percent lead to significant blue shift of the reflected colors making these films excellent candidates for applications as deformation sensors. Higher strains up to 90% lead to a tremendous Bragg reflection color change caused by transition from the (111) to the (200) lattice plane. The well-ordered opaline structure with its stop band at the emission frequency of the incorporated fluorescent dye shows remarkable angle-dependent fluorescence suppression. Herein described elastomeric opal films can be valuable in a wide range of applications such as rewritable 3D optical data storage, tunable laser action, and sensing materials.

Nanocapsules composed of a poly(vinylferrocene)-block-poly(methyl methacrylate) shell and a hydrophobic liquid core are prepared in water. The nanocapsule shells display a patchy structure with poly(vinylferrocene) patches with sizes of 25 ± 3 nm surrounded by poly(methyl methacrylate). The functional nanopatches can be selectively oxidized, thereby influencing the colloidal morphology and introducing polar domains in the nanocapsule shell. The hydrophobic to hydrophilic transition in the redox-responsive nanopatches can be advantageously used to release a hydrophobic payload encapsulated in the core by an oxidation reaction.

Asymmetric Faradaic system based on organometallic electrodes shows suppression of parasitic water reactions and remarkable selectivity in redox-mediated electrosorption of micropollutants.

Well-defined poly(2-(methacryloyloxy)ethyl ferrocenecarboxylate) (PFcMA) brushes were synthesized by surface-initiated atom transfer radical polymerization (SI-ATRP) on cross-linked polystyrene particles. The ATRP of FcMA monomer was reinvestigated leading to molar masses up to 130 kg mol–1 with a good reaction control and high monomer conversion (91%). The SI-ATRP was done with different amounts of initiator in the PS particle shell leading to PFcMA surface conformations from “mushroom-like” to dense “brush-like” polymers, which could be confirmed by dynamic light scattering (DLS) experiments. Redox-responsive behavior of the PFcMA shell was investigated by DLS and cyclic voltammetry (CV) measurements indicating a tremendous increase in the hydrodynamic volume of the ferrocene-containing shell. The transformation of PFcMA-grafted PS particles to magnetic iron oxides after thermal treatment could be investigated by SQUID magnetization measurements showing the typical hysteresis for ferromagnetic material.

The living anionic copolymerization of isoprene and styrene in cyclohexane affords tapered block copolymers due to the highly disparate reactivity ratios of r I = 12.8 and r S = 0.051. Repeated addition of a mixture of these monomers was exploited to generate tapered multiblock copolymer architectures of the (AB) n type with up to 10 blocks (1 ≤ n ≤ 5), thereby subdividing the polymer chains in alternating flexible polyisoprene (PI) and rigid polystyrene (PS) segments. Three series of well-defined tapered multiblock copolymers with approximate molecular weights of 80, 240, and 400 kg/mol were prepared on the 100 g scale. Via this synthetic strategy polymer chains were divided in di-, tetra-, hexa-, octa-, and decablock tapered multiblock structures. Because of the living nature of the polymerization, low dispersities in the range 1.06–1.28 (decablock) were obtained. To ensure full monomer conversion prior to the addition of the isoprene/styrene mixture, kinetic Monte Carlo simulation was employed, permitting to simulate chain growth in silico by employing the known polymerization rates and rate constants k p. The synthesized tapered multiblock copolymers were characterized via SEC and selected samples via oxidative degradation of the polyisoprene block in solution, confirming the well-defined nature of the PS segments. Subsequently, the question was addressed, to which extent the tapered multiblock copolymers are capable of forming ordered nanosegregated morphologies. Detailed thermal, structural, and rheological investigations showed that the tapered multiblock copolymers with a molecular weight of 240 kg/mol formed ordered phases with the expected lamellar morphology. However, X-ray scattering data and transmission electron microscopy (TEM) images of the octablock and decablock copolymers reflect weakly ordered structures at ambient temperature. The domain spacing, d, was found to scale as d ∼ N 0.62, where N is the total degree of polymerization, suggesting stretching of chains and nonideal configurations. Following the structure factor, S(q), as a function of temperature revealed that the tapered multiblock copolymers undergo a fluctuation-induced first-order transition at the respective order-to-disorder transition temperature, T ODT. The viscoelastic response of the tapered copolymers was controlled by the nanodomain structure, the degree of segregation, nanodomain-bridging configurations of blocks, and also the proximity to the glass temperature of the vitrified PS domains. Tapered hexablock copolymers were found to best combine structural integrity and mechanical toughness, while maintaining a large strain at break (>900%).

Redox-responsive nanocapsules consisting of conductive polyaniline and polypyrrole shells were successfully synthesized by using the interface of miniemulsion droplets as a template for oxidative polymerizations. The redox properties of the capsules were investigated by optical spectroscopies, electron microscopy, and cyclic voltammetry. Self-healing (SH) chemicals such as diglycidyl ether or dicarboxylic acid terminated polydimethylsiloxane (PDMS-DE or PDMS-DC) were encapsulated into the nanocapsules during the miniemulsion process and their redox-responsive release was monitored by (1)H NMR spectroscopy. The polyaniline capsules exhibited delayed release under oxidation and rapid release under reduction, which make them promising candidates for anticorrosion applications.

Little advantage has been taken so far of the manifold promising options provided by the living anionic polymerization of vinylferrocene. The major reason is that the propagating polyvinylferrocene (PVFc) chains suffer loss of reactivity in the oligomeric state already, and even can change into a “sleeping” mode prior to complete monomer consumption. Formation of broadly distributed and/or constitutionally inhomogeneous products is the consequence. Here we report on the efficient reactivation of the deactivated or sleeping PVFc macro-anions by their simultaneous treatment with 1,1-dimethylsilacyclobutane and 1,1-diphenylethylene. We demonstrate the efficiency of this procedure by synthesizing PVFc-based diblock copolymers with poly(methyl methacrylate) and poly(2-vinylpyridine), respectively, using sequential monomer addition protocols.

Block copolymers of polyisoprene and polystyrene are key materials for polymer nanostructures as well as for several commercially established thermoplastic elastomers. In a combined experimental and kinetic Monte Carlo simulation study, the direct (i.e., statistical) living anionic copolymerization of a mixture of isoprene (I) and 4-methylstyrene (4MS) in nonpolar media was investigated on a fundamental level. In situ 1 H NMR spectroscopy enabled to directly monitor gradient formation during the copolymerization and to determine the nature of the gradient. In addition, a precise comparison with the established copolymerization of isoprene and styrene (I/S) was possible. Statistical copolymerization in both systems leads to tapered block copolymers due to an extremely slow crossover from isoprene to the styrenic monomer. For the system I/4MS the determination of the reactivity ratios shows highly disparate values with r I = 25.4 and r 4MS = 0.007, resulting in a steep gradient of the comonomer composition. The rate constants determined from online NMR studies were used for a kinetic Monte Carlo simulation, revealing structural details, such as the distribution of the homopolymer sequences for both blocks, which are a consequence of the peculiar kinetics of the diene/styrene systems. DFT calculations were used to compare the established copolymerization of isoprene and styrene with the isoprene/4-methylstyrene system. A variety of gradient copolymers differing in molecular weight and monomer feed composition were synthesized, confirming strong microphase segregation as a consequence of the blocklike structure. The one-pot synthesis of such tapered block copolymers, avoiding high vacuum or break-seal techniques, is a key advantage for the preparation of ultrahigh molecular weight block copolymers (M n > 1.2 × 10 6 g/mol) in one synthetic step. These materials show microphase-segregated bulk structures like diblock copolymers prepared by sequential block copolymer synthesis. Because of the living nature of the tapered block copolymer structures, a vast variety of complex structures are accessible by the addition of further monomers or monomer mixtures in subsequent steps.