Water, when confined at the nanoscale acquires extraordinary transport properties, and yet, there is no direct experimental evidence of these properties at nanoscale resolution. Here, by using two-dimensional NMR diffusion–relaxation (D–T 2) and spin–lattice – spin–spin relaxation (T 1–T 2) spectroscopy, we succeeded to resolve at the nanoscale water diffusion in single- and double-walled carbon nanotubes (SWCNTs/DWCNTs). In SWCNTs, the spectra display the characteristic shape of uniform water diffusion restricted in one dimension. Remarkably, in DWCNTs, water is shown to split into two axial components with the inner one acquiring unusual flow properties: high fragility, ultrafast self-diffusion coefficient, and “rigid” molecular environment, revealing a stratified cooperative motion mechanism to underlie fast diffusion in water-saturated CNTs.

Sulfur copolymers with high sulfur content find a broad range of applications from Li–S batteries to catalytic processes, self-healing materials, and the synthesis of nanoparticles. Synthesis of sulfur-containing polymers via the inverse vulcanization technique gained a lot of attention due to the feasibility of the reaction to produce copolymers with high sulfur content (up to 90 wt %). However, the interplay between the cross-linker and the structure of the copolymers has not yet been fully explored. In the present work, the effect of the amount of 1,3-diisopropenyl benzene (DIB) cross-linker on the structural stability of the copolymer was thoroughly investigated. Combining X-ray diffraction and differential scanning calorimetry, we demonstrated the partial depolymerization of sulfur in the copolymer containing low amount of cross-linker (<30 wt % DIB). On the other hand, by applying NMR and electron paramagnetic resonance techniques, we have shown that increasing the cross-linker content above 50 wt % leads to the formation of radicals, which may severely degrade the structural stability of the copolymer. Thus, an optimum amount of cross-linker is essential to obtain a stable copolymer. Moreover, we were able to detect the release of H 2 S gas during the cross-linking reaction as predicted based on the abstraction of hydrogen by the sulfur radicals and therefore we emphasize the need to take appropriate precautions while implementing the inverse vulcanization reaction.

It is well known that water inside hydrophobic nano-channels diffuses faster than bulk water. Recent theoretical studies have shown that this enhancement depends on the size of the hydrophobic nanochannels. However, experimental evidence of this dependence is lacking. Here, by combining two-dimensional nuclear magnetic resonance diffusion–relaxation (D–T2eff) spectroscopy in the stray field of a superconducting magnet and molecular dynamics simulations, we analyze the size dependence of water dynamics inside Carbon Nanotubes (CNTs) of different diameters (1.1–6.0 nm), in the temperature range of 265–305 K. Depending on the CNT diameter, the nanotube water is shown to resolve in two or more tubular components acquiring different self-diffusion coefficients. Most notably, a favorable CNT diameter range (3.0–4.5 nm) is experimentally verified for the first time, in which water molecule dynamics at the center of the CNTs exhibits distinctly non-Arrhenius behavior, characterized by ultrafast diffusion and extraordinary fragility, a result of significant importance in the efforts to understand water behavior in hydrophobic nanochannels.

Structural and morphological control of crystalline nanoparticles is crucial in the field of heterogeneous catalysis and the development of “reaction specific” catalysts. To achieve this, colloidal chemistry methods are combined with ab initio calculations in order to define the reaction parameters, which drive chemical reactions to the desired crystal nucleation and growth path. Key in this procedure is the experimental verification of the predicted crystal facets and their corresponding electronic structure, which in case of nanostructured materials becomes extremely difficult. Here, by employing 31P solid-state nuclear magnetic resonance aided by advanced density functional theory calculations to obtain and assign the Knight shifts, we succeed in determining the crystal and electronic structure of the terminating surfaces of ultrafine Ni2P nanoparticles at atomic scale resolution. Our work highlights the potential of ssNMR nanocrystallography as a unique tool in the emerging field of facet-engineered nanocatalysts.

Highly active nickel phosphide (Ni2P) nanoclusters confined in a mesoporous SiO2 catalyst were synthesized by a two-step process targeting tight control over the Ni2P size and phase. The Ni precursor was incorporated into the MCM-41 matrix by one-pot synthesis, followed by the phosphorization step, which was accomplished in oleylamine with trioctylphosphine at 300 °C so to achieve the phase transformation from Ni to Ni2P. For benchmarking, Ni confined by the mesoporous SiO2 (absence of phosphorization) and 11 nm Ni2P nanoparticles (absence of SiO2) was also prepared. From the microstructural analysis, it was found that the growth of Ni2P nanoclusters was restricted by the mesoporous channels, thus forming ultrafine and highly dispersed Ni2P nanoclusters (<2 nm). The above approach led to promising catalytic performance following the order u-Ni2P@m-SiO2 > n-Ni2P > u-Ni@m-SiO2 > c-Ni2P in the selective hydrogenation of SO2 to S. In particular, u-Ni2P@m-SiO2 exhibited SO2 conversions of 94% at 220 °C and ∼99% at 240 °C, which are higher than the 11 nm stand-alone Ni2P particles (43% at 220 °C and 94% at 320 °C), highlighting the importance of the role played by SiO2 in stabilizing ultrafine nanoparticles of Ni2P. The reaction activation energy E a over u-Ni2P@m-SiO2 is ∼33 kJ/mol, which is lower than those over n-Ni2P (∼36 kJ/mol) and c-Ni2P (∼66 kJ/mol), suggesting that the reaction becomes energetically favored over the ultrafine Ni2P nanoclusters.