Measurements of rates of dissolution of typical insulation wool fibers (glasswool and basalt based stonewool) and an experimental fiber were made using a flow-through equipment. The liquids used were a modified Gamble's solution, adjusted to pH 4.8 and 7.7 +/- 0.2, respectively. The dissolution of SiO2 and CaO was determined over periods of up to three months. The rate of dissolution of stonewool fibers was lower than that of glasswool fibers at pH 7.7, whereas the opposite was true at pH 4.8. The stonewool fibers dissolve congruently, but glasswool fibers tend to dissolve with leaching. The rates of dissolution of fibers of different compositions, including insulation wool (glasswool, basalt-based stonewool, slagwool) and experimental fibers were screened using a stationary set-up. Both the chemical composition and pH influenced the rates of dissolution. At pH 7.7 alumina was a determining component and at pH 4.8 the content of SiO2 and CaO was determinant. One experimental fiber with a high content of alumina was an exception having a fairly high rate of dissolution both at pH 4.8 and 7.7.
In order to determine whether breakage of long vitreous fibers in the lung could be responsible for removing significant numbers of these fibers, an intratracheal instillation study was done with a preparation consisting of mostly long fibers of two different types. Following instillation of both fibers, laboratory rats were sacrificed at 6 times up to 14 days. The NK (conventional borosilicate glass) fiber preparation had about 20% short fibers (length < or = 15 microm) initially, and fibers recovered from the lungs remained at that proportion for the entire 14 days. But the HT (a new rock or stone wool) fiber preparation, which had about 5% short fibers initially, jumped to about 50% short fibers at 2 days and remained at that proportion for the rest of the study. The appearance of many short HT fibers where there were few initially is conclusive evidence that these long fibers break, and it explains their rapid removal from the lung. Since the HT fibers dissolve rapidly at acid pH, but slowly at the near neutral pH of the extracellular lung fluid, it is likely that acid attack by phagocytic cells is causing the long fibers to dissolve and break. The long NK fibers dissolve rapidly at neutral pH but slowly at acid pH and thus appear to clear by more or less uniform dissolution without apparent breakage. The long fibers of these two kinds are removed rapidly at about the same rate, but by a different mechanism.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.