In this study, polyethylene glycol-modified titanium dioxide (PEG-modified TiO2) nanopowders were prepared using a fast solvothermal method under microwave irradiation, and without any further calcination processes. These nanopowders were further impregnated on porous polymeric platforms by drop-casting. The effect of adding iron with different molar ratios (1, 2, and 5%) of iron precursor was investigated. The characterization of the produced materials was carried out by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Raman spectroscopy. Optical characterization of all the materials was also carried out. SEM showed that pure TiO2 and Fe-TiO2 nanostructures presented similar nanosized and spherical particles, which uniformly covered the substrates. From XRD, pure TiO2 anatase was obtained for all nanopowders produced, which was further confirmed by Raman spectroscopy on the impregnated substrates. XPS and UV–VIS absorption spectroscopy emission spectra revealed that the presence of Fe ions on the Fe-TiO2 nanostructures led to the introduction of new intermediate energy levels, as well as defects that contributed to an enhancement in the photocatalytic performance. The photocatalytic results under solar radiation demonstrated increased photocatalytic activity in the presence of the 5% Fe-TiO2 nanostructures (Rhodamine B degradation of 85% after 3.5 h, compared to 74% with pure TiO2 for the same exposure time). The photodegradation rate of RhB dye with the Fe-TiO2 substrate was 1.5-times faster than pure TiO2. Reusability tests were also performed. The approach developed in this work originated novel functionalized photocatalytic platforms, which were revealed to be promising for the removal of organic dyes from wastewater.
In the present study, titanium dioxide (TiO2) nano-photocatalysts were synthesized through microwave irradiation. In a typical microwave synthesis, TiO2 nanomaterials were simultaneously produced in powder form and also directly covering cork substrates. The TiO2 nanopowder was analyzed by X-ray diffraction (XRD), Raman spectroscopy and transmission electron microscopy (TEM), revealing that the solvothermal microwave synthesis resulted only in the TiO2 anatase phase. From Fourier-transform infrared spectroscopy (FTIR), cork’s organic species, along with bands of TiO2, were detected. UV–VIS absorption spectrum revealed an absorption extension to the visible region, since a brown powdered TiO2 product was obtained. Very fine nanoparticles were observed displaying a nearly spherical shape that agglomerates in larger particles. These larger particles fully covered the surface of the honeycomb cork cells, originating TiO2 functionalized cork platforms. The TiO2 functionalized substrates were further tested as floating photocatalysts and their photocatalytic activity was assessed from rhodamine B degradation under solar simulating light and natural sunlight. Reusability tests were also performed under natural sunlight. The strategy applied in this research work allowed the production of green and low-cost cork platforms based on TiO2 photoactive materials with the ability to purify polluted water under natural sunlight.
The present study is focused on the synthesis of zirconium dioxide (ZrO2) nanomaterials using the hydrothermal method assisted by microwave irradiation and solution combustion synthesis. Both synthesis techniques resulted in ZrO2 powders with a mixture of tetragonal and monoclinic phases. For microwave synthesis, a further calcination treatment at 800 °C for 15 min was carried out to produce nanopowders with a dominant monoclinic ZrO2 phase, as attested by X-ray diffraction (XRD) and Raman spectroscopy. The thermal behavior of the ZrO2 nanopowder was investigated by in situ XRD measurements. From the scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images, the presence of near spherical nanoparticles was clear, and TEM confirmed the ZrO2 phases that comprised the calcinated nanopowders, which include a residual tetragonal phase. The optical properties of these ZrO2 nanopowders were assessed through photoluminescence (PL) and PL excitation (PLE) at room temperature (RT), revealing the presence of a broad emission band peaked in the visible spectral region, which suffers a redshift in its peak position, as well as intensity enhancement, after the calcination treatment. The powder resultant from the solution combustion synthesis was composed of plate-like structures with a micrometer size; however, ZrO2 nanoparticles with different shapes were also observed. Thin films were also produced by solution combustion synthesis and deposited on silicon substrates to produce energy storage devices, i.e., ZrO2 capacitors. The capacitors that were prepared from a 0.2 M zirconium nitrate-based precursor solution in 2-methoxyethanol and annealed at 350 °C exhibited an average dielectric constant (κ) of 11 ± 0.5 and low leakage current density of 3.9 ± 1.1 × 10−7 A/cm2 at 1 MV/cm. This study demonstrates the simple and cost-effective aspects of both synthesis routes to produce ZrO2 nanomaterials that can be applied to energy storage devices, such as capacitors.
The preparation of visible-light-driven photocatalysts has become highly appealing for environmental remediation through simple, fast and green chemical methods. The current study reports the synthesis and characterization of graphitic carbon nitride/titanium dioxide (g-C3N4/TiO2) heterostructures through a fast (1 h) and simple microwave-assisted approach. Different g-C3N4 amounts mixed with TiO2 (15, 30 and 45 wt. %) were investigated for the photocatalytic degradation of a recalcitrant azo dye (methyl orange (MO)) under solar simulating light. X-ray diffraction (XRD) revealed the anatase TiO2 phase for the pure material and all heterostructures produced. Scanning electron microscopy (SEM) showed that by increasing the amount of g-C3N4 in the synthesis, large TiO2 aggregates composed of irregularly shaped particles were disintegrated and resulted in smaller ones, composing a film that covered the g-C3N4 nanosheets. Scanning transmission electron microscopy (STEM) analyses confirmed the existence of an effective interface between a g-C3N4 nanosheet and a TiO2 nanocrystal. X-ray photoelectron spectroscopy (XPS) evidenced no chemical alterations to both g-C3N4 and TiO2 at the heterostructure. The visible-light absorption shift was indicated by the red shift in the absorption onset through the ultraviolet-visible (UV-VIS) absorption spectra. The 30 wt. % of g-C3N4/TiO2 heterostructure showed the best photocatalytic performance, with a MO dye degradation of 85% in 4 h, corresponding to an enhanced efficiency of almost 2 and 10 times greater than that of pure TiO2 and g-C3N4 nanosheets, respectively. Superoxide radical species were found to be the most active radical species in the MO photodegradation process. The creation of a type-II heterostructure is highly suggested due to the negligible participation of hydroxyl radical species in the photodegradation process. The superior photocatalytic activity was attributed to the synergy of g-C3N4 and TiO2 materials.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.