The aim of this paper was to prepare a poly (vinylidene fluoride) (PVDF) membrane using different non-solvents in the coagulation bath for the phase inversion method. In order to increase the mechanical strength of membranes, facing the pressure of work, was used a macro-porous polyester support. The morphology and structure of the resulting membranes were evaluated by scanning electron microscopy, porosity measurements, water and 1-octanol uptake, contact angle, pure water flux, hydraulic permeability and hydraulic resistance. The morphology and pure water flux changed significantly using ethanol (symmetric membrane) and/or water (asymmetric membrane) as the non-solvent. The symmetric membrane presented a high hydrophobic surface (water contact angle ~136°) and a higher pure water flux and porosity than the asymmetric membrane, which presented a lower hydrophobicity surface (water contact angle ~90°). The morphologies obtained suggest different applications.

No abstract

Resumo: O poli(fluoreto de vinilideno) (PVDF) é um polímero semicristalino contendo uma fase amorfa e uma cristalina. Essa característica é importante para o preparo de membranas assimétricas, pois a fase cristalina tem grande influência na formação da estrutura da membrana e a fase amorfa na porosidade. Membranas de PVDF foram preparadas pelo processo de inversão de fases e avaliadas quanto à permeabilidade e morfologia, bem como o efeito do tratamento térmico. Foram comparadas as seguintes membranas: membrana sem tratamento térmico, membrana com tratamento térmico e membrana comercial. Ensaios de resistência química, fluxo permeado de água a várias pressões, difusão de íons, Microscopia Eletrônica de Varredura (MEV), Calorimetria Exploratória Diferencial (DSC) e Análise Termogravimétrica (TGA) foram realizados para verificar o comportamento das membranas. Palavras-chave: PVDF, tratamento térmico, inversão de fases, membrana polimérica. Preparation and Characterization of Asymmetric Membranes of Poly (Vinylidene Fluoride) Supported in Polyester -I: Effect of Heat Treatment in the Properties of MembranesAbstract: Poly(Vinylidene Fluoride) (PVDF) is a semicrystalline polymer containing an amorphous and a crystalline phase. This characteristic is important for the preparation of asymmetric membranes, because the crystalline phase has great influence on the membranes structure, while the amorphous phase affects the porosity. PVDF membranes were prepared by the phase inversion process, which were then evaluated with regard to permeability and morphology, as well as the thermal treatment effect. The following membranes were compared: without thermal treatment, with thermal treatment and commercially-available membrane. The analysis of chemical resistance, water permeability flux to different pressures and diffusion of ions, in addition to studies with Scanning Electron Microscopy (SEM), Differential Scanning Calorimetry (DSC) and Thermogravimetric Analysis (TGA), were performed to investigate the membranes properties.