Increased surface roughness of dental implants has demonstrated greater bone apposition; however, the effect of modifying surface chemistry remains unknown. In the present study, we evaluated bone apposition to a modified sandblasted/acid-etched (modSLA) titanium surface, as compared with a standard SLA surface, during early stages of bone regeneration. Experimental implants were placed in miniature pigs, creating 2 circular bone defects. Test and control implants had the same topography, but differed in surface chemistry. We created the test surface by submerging the implant in an isotonic NaCl solution following acid-etching to avoid contamination with molecules from the atmosphere. Test implants demonstrated a significantly greater mean percentage of bone-implant contact as compared with controls at 2 (49.30 vs. 29.42%; p = 0.017) and 4 wks (81.91 vs. 66.57%; p = 0.011) of healing. At 8 wks, similar results were observed. It is concluded that the modSLA surface promoted enhanced bone apposition during early stages of bone regeneration.

Titanium (Ti) is used for implantable devices because of its biocompatible oxide surface layer. TiO2 surfaces that have a complex microtopography increase bone-to-implant contact and removal torque forces in vivo and induce osteoblast differentiation in vitro. Studies examining osteoblast response to controlled surface chemistries indicate that hydrophilic surfaces are osteogenic, but TiO2 surfaces produced until now exhibit low surface energy because of adsorbed hydrocarbons and carbonates from the ambient atmosphere or roughness induced hydrophobicity. Novel hydroxylated/hydrated Ti surfaces were used to retain high surface energy of TiO2. Osteoblasts grown on this modified surface exhibited a more differentiated phenotype characterized by increased alkaline phosphatase activity and osteocalcin and generated an osteogenic microenvironment through higher production of PGE2 and TGF-beta1. Moreover, 1alpha,25OH2D3 increased these effects in a manner that was synergistic with high surface energy. This suggests that increased bone formation observed on modified Ti surfaces in vivo is due in part to stimulatory effects of high surface energy on osteoblasts.

Roughness-induced hydrophobicity, well-known from natural plant surfaces and intensively studied toward superhydrophobic surfaces, has currently been identified on microstructured titanium implant surfaces. Studies indicate that microstructuring by sandblasting and acid etching (SLA) enhances the osteogenic properties of titanium. The undesired initial hydrophobicity, however, presumably decelerates primary interactions with the aqueous biosystem. To improve the initial wettability and to retain SLA microstructure, a novel surface modification was tested. This modification differs from SLA by its preparation after acid etching, which was done under protective gas conditions following liquid instead of dry storage. We hypothesized that this modification should have increased wettability due to the prevention of contaminations that occurs during air contact. The main outcome of dynamic wettability measurements was that the novel modification shows increased surface free energy (SFE) and increased hydrophilicity with initial water contact angles of 0 degrees compared to 139.9 degrees for SLA. This hydrophilization was kept even after any drying. Reduced hydrocarbon contaminations were identified to play a possible role in altered surface thermodynamics. Such surfaces aim to retain the hydrophilicity and natural high surface energy of the Ti dioxide surface until surgical implants' insertion and are compared in this in vitro study with structural surface variants of titanium to compare roughness and chemically induced wettability.