Dealumination of NH(4)-Y zeolite during steaming to 873 K was investigated with in situ, time-dependent, synchrotron radiation XRPD and in situ Al K-edge XAS. Water desorption is complete at 450 K, and ammonium decomposition occurs between 500 and 550 K. Only a small fraction of Al(3+) species (5%) leaves the framework during heating from 710 to 873 K; these species occupy site I' inside the sodalite cage. This fraction increases up to 8% in the first 50 min at 873 K and remains constant for the following 70 min isotherm and during the high-temperature part of the cooling experiment. During cooling from 500 to 450 K, the electron density at site I' increases suddenly, corresponding to a fraction of 30-35% of the total Al, confirmed by ex situ (27)Al MAS solid-state NMR. At that temperature, in situ Al K-edge XAS indicates a change in Al coordination of a large fraction of Al, and thermogravimetric (TG) data show the first water molecules start to repopulate the pores. Such molecules drive the dislodgment of most of the Al from the zeolitic framework. Our data indicate that considerable structural collapse caused by steaming does not occur at the highest temperature; however, defects form, which lead to significant migration of framework Al(3+) to extraframework positions, which occurs only as water is able to enter the pores again, that is, at much lower temperature. Contrary to general opinion, these results demonstrate that zeolite dealumination is not primarily a high-temperature process. The standard Rietveld refinement approach failed to identify extraframework Al species. These new results were obtained by adopting the innovative parametric refinement [J. Appl. Crystallogr. 2007, 40, 87]. Treating all of the XRPD patterns collected during the evolution of temperature as one unique data set significantly reduces the overall number of optimized variables and, thus, their relative correlation, and finally results in a more reliable estimate of the optimized parameters. Our results contribute to a better understanding of the phenomena involved on the atomic scale in the preparation of ultrastable Y zeolites (USY). USY are employed in fluid catalytic cracking (FCC), which is the most important conversion process in petroleum refineries to convert the high-boiling hydrocarbon fractions of petroleum crude oils to more valuable products like gasoline and olefinic gases.

The crystalline State and isometric Operations 1 Symmetry elements 3 Axes of rotational symmetry 3 Axes of rototranslation or screw axes 5 Axes of inversion 5 Axes of rotorefiection 5 Refiection planes with translational component (glide planes) 6 Lattices 6 The rational properties of lattices 7 Crystallographic directions 7 Crystallographic planes 8 Symmetry restrictions due to the lattice periodicity and vice versa 9 Point groups and symmetry classes 11 Point groups in one and two dimensions 16 The Laue classes 17 The seven crystal Systems 17 The Bravais lattices 18 Plane lattices 18 Space lattices 19 The space groups 22 The plane and line groups 30 On the matrix representation of symmetry Operators 32 Appendices: LA The isometric transformations 35 l.B Some combinations of movements 37 l.C Wigner-Seitz cells 41 l.D The space-group rotation matrices l.E Symmetry groups l.F Symmetry generalization References Crystallographic Computing Carmelo Giacovazzo

The structure of [Fe(Htrz) 2 (trz)]BF 4 (1, Htrz )1,2,4-4-H-triazole, trz ) 1,2,4-triazolate) at the low-spin (LS) and high-spin (HS) states and structural transitions between the two states were investigated by in situ highresolution synchrotron X-ray powder diffraction (XRPD) combined with Raman spectroscopy using a modulation-enhanced technique. The crystal structures of the LS and HS states were determined. A 1D chain structure of 1 at both LS and HS states was proven, and the lattice expansion upon LS-HS transition was mainly caused by the elongation of the chain. The differences in the behavior of the spin transition observed by XRPD and Raman spectroscopy were explained by the local sensitivity of the two different techniques and also by the spatial propagation of spin crossover phase transition within the crystallite and the body of the grain. Moreover, we demonstrated that the two-dimensional correlation analyses facilitate (i) understanding the data obtained by combined techniques, (ii) clarifying correlation between the signals gained by the different probes, and (iii) extracting information on temporal evolution of transformation processes.

The heating process (30-200 QC) of a paly gorskite-indigo mixture has been monitored in situ and simultaneously by synchrotron powder diffraction and Raman spectroscopy. During this process, the dye and the clay interact to form Maya blue (MB), a pigment highly resistant to degradation . It is shown that the formation of a very stable pigment occurs in the 70-130 QC interval; i.e., when palygorskite starts to loose zeolitic water, and is accompanied by a reduction of the crystallographic a parameter, as well as by alterations in the C=C and C=O bonds of indigo. Mid-and near-infrared spectroscopic work and rnicroporosity measurements, employed to study the rehydration process after the complex formation, pro vide evidence for the inhibition of the rehydration of l\1B as compared with palygorskite. These results are consistent with the blocking of the palygorskite tunnel entrance by indigo molecules with a possible partial penetration inside the tunnels. The surface silanols of palygorskite are not perturbed by indigo, suggesting that MB is not a surface complex.

Siliceous sponges, one of the few animal groups involved in a biosilicification process, deposit hydrated silica in discrete skeletal elements called spicules. A multidisciplinary analysis of the structural features of the protein axial filaments inside the spicules of a number of marine sponges, belonging to two different classes (Demospongiae and Hexactinellida), is presented, together with a preliminary analysis of the biosilicification process. The study was carried out by a unique combination of techniques: fiber diffraction using synchrotron radiation, scanning electron microscopy (SEM), thermogravimetric analysis (TGA), differential scanning calorimetric (DSC), Fourier transform infrared spectroscopy (FTIR), and molecular modeling. From a phylogenetic point of view, the main result is the structural difference between the dimension and packing of the protein units in the spicule filaments of the Demospongiae and the Hexactinellida species. Models of the protein organization in the spicule axial filaments, consistent with the various experimental evidences, are given. The three different species of demosponges analyzed have similar general structural features, but they differ in the degree of order. The structural information on the spicule axial filaments can help shed some light on the still unknown molecular mechanisms controlling biosilicification.

The high X-ray flux available at the European Synchrotron Radiation Facility (ESRF), combined with the use of a suitably designed area detector setup, allowed us to follow in real time the structural changes occurring during the template burning processes inside TS-1 and Fe-silicalite MFI zeolites with a X-ray powder diffraction technique (XRPD). Rietveld analysis of the XRPD patterns collected in the 350-1000 K interval, integrated each 15 K, yields to the determination of the template overall occupancy factor versus T with an accuracy comparable with that obtained by thermogravimetric measurements, routinely employed for this purpose. The evolution of the structural parameters (V, a, b, c, site occupancy factor of the template molecule) vs T has been obtained. These data allow us to have, for the first time, a complete view of the structural rearrangements induced by the template burning process on the zeolitic framework. The differences caused by the different heteroatom inserted in the MFI lattice (Ti or Fe) are discussed. For both TS-1 and Fe-MFI, the kinetics of the reaction were investigated, to obtain the activation energy of the calcinations process employing the nonisothermal data according to the theory recently proposed by Kennedy and Clark [Thermochim. Acta, 1997, 307, 27-35]. For TS-1 only, the time-resolved template burning experiment has been repeated in isothermal conditions at four different temperatures, to obtain the activation energy from isothermal data, according to the standard procedure. Comparison between Arrhenius plots obtained from isothermal and nonisothermal data demonstrates that the Kennedy and Clark method can be also applied to complex materials such as the MFI zeolites. This approach, when applied to time-resolved XRPD studies, is much less time consuming (requesting, in principle, one single nonisothermal run) with respect to the classic approach, which requests at least three isothermal runs. Moreover, it allows a remarkably lower associated error (151 +/- 11 versus 146 +/- 30 kJ mol(-)(1)) due to the much higher number of experimental points employed to perform the linear fit.

A theory is developed to describe the kinematic diffraction response of a crystal when it is subjected to a periodically varying external perturbation. It is shown that if a part of the local electron density varies linearly with an external stimulus, the diffracted signal is not only a function of the stimulation frequency Ω, but also of its double 2Ω. These frequency components can provide, under certain conditions, selective access to partial diffraction contributions that are normally summed up in the interference pattern. A phasing process applied to partial diffraction terms would allow recovery of the substructure actively responding to the stimulus. Two ways of frequency filtering are discussed (demodulation and correlation) with respect to extracting information from such an experiment. Also considered is the effect of the variation of different structural parameters on the diffraction intensity that have to be accounted for while planning modulation-enhanced experiments. Finally, the advantages and limitations of the proposed concept are discussed, together with possible experiments.

No abstract