In this animal model, a biomimetic calcium phosphate coating gave similar osseointegration to the SLA surface. This biomimetic coating method may enhance the apposition of bone onto titanium dental implants.
Two porous titanium implants with a pore size diameter of 800 and 1200 microm (Ti800 and Ti1200) and an interconnected network were manufactured using rapid prototyping. Their dimensions and structure matched those of the computer assisted design. The porosity of the implants was around 60%. Their compressive strength and Young's modulus were around 80 MPa and 2.7 GPa, respectively. These values are comparable to those of cortical bone. The implants were implanted bilaterally in the femoral epiphysis of 15 New Zealand White rabbits. After 3 and 8 weeks, abundant bone formation was found inside the rapid prototyped porous titanium implants. For the Ti1200 implants, bone ingrowth was (23.9 +/- 3.5)% and (10.3 +/- 2.8)%, respectively. A significant statistical difference (p < 0.05) was found for bone ingrowth in the Ti1200 between the two delays. The percentage of bone directly apposited on titanium was (35.8 +/- 5.4)% and (30.5 +/- 5.0)%. No significant difference was found for bone-implant contact between the different time periods and pore sizes. This work demonstrates that manufacturing macroporous titanium implants with controlled shape and porosity using a rapid prototyping method is possible and that this technique is a good candidate for orthopedic and maxillofacial applications.
Silicate bioceramics possess an excellent bioactivity; however, shaping them into complex geometries is still challenging. Therefore, this paper aims to present a new strategy for the shaping of a bioglass-ceramic with controlled geometry and properties starting from a glass powder combined with a preceramic polymer, i.e. a silicon resin, and reactive fillers. The powder-based three-dimensional (3D)-printing of wollastonite (CaSiO3)-based silicate bioceramic parts was demonstrated in this work. The resin plays a dual role, as it not only acts as a non-sacrificial binder for the filler powders in the printing process but it also reacts with the fillers to generate the desired bioceramic phases. The mechanical and physical properties, i.e. ball-on-three-balls test, density, porosity and morphology, were evaluated in 3D-printed discs. These samples possessed a total porosity around 64 vol% and a biaxial flexural strength around 6 MPa. The raw materials used in this work also enabled the 3D-printing of scaffolds possessing a designed multi-scale porosity, suitable bioceramic phase assemblage and a compressive strength of 1 MPa (for cylindrical scaffolds with total porosity ~80 vol%). Solubility in TRIS/HCl and in vitro assays, i.e. viability, cytotoxicity and apoptosis assays, were also performed. In vitro tests indicated good cell viability and no cytotoxicity effect on the cells.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.