Photosensitive alkoxyamine 2,2,6,6-tetramethyl-1-(1-phenylethoxy)piperidin-4-yl quinoline-2-carboxylate (PE-TEMPO-Q) was synthesized. Photochemical properties of PE-TEMPO-Q were studied to develop photoinduced nitroxide-mediated polymerization of methyl methacrylate (MMA). Rapid and facile polymerization at ambient temperature with PE-TEMPO-Q as an initiator was confirmed to proceed in a controlled mechanism based on the linear growth in molecular weight combined with relative narrow polydispersity index (1.4-1.8) of the resulting polymers. The stereochemistry of obtained polymers was also investigated, and the syndiotacticity slightly increased compared with the typical photopolymerization. Dual-controlled photopolymerization of MMA was achieved in the presence of synthesized alkoxyamine.

To improve the interfacial compatibility of mixed matrix membranes (MMMs) for gas separation, microporous polyimide particle (AP) was designed, synthesized, and introduced into intrinsic microporous polyimide matrix (6FDA-Durene) to form “all polyimide” MMMs. The AP fillers showed the feature of thermal stability, similar density with polyimide matrix, high porosity, high fractional free volume, large microporous dimension, and interpenetrating network architecture. As expected, the excellent interfacial compatibility between 6FDA-Durene and AP without obvious agglomeration even at a high AP loading of 10 wt.% was observed. As a result, the CO2 permeability coefficient of MMM with AP loading as low as 5 wt.% reaches up to 1291.13 Barrer, which is 2.58 times that of the pristine 6FDA-Durene membrane without the significant sacrificing of ideal selectivity of CO2/CH4. The improvement of permeability properties is much better than that of the previously reported MMMs, where high filler content is required to achieve a high permeability increase but usually leads to significant agglomeration or phase separation of fillers. It is believed that the excellent interfacial compatibility between the PI fillers and the PI matrix induce the effective utilization of porosity and free volume of AP fillers during gas transport. Thus, a higher diffusion coefficient of MMMs has been observed than that of the pristine PI membrane. Furthermore, the rigid polyimide fillers also result in the excellent anti-plasticization ability for CO2. The MMMs with a 10 wt.% AP loading shows a CO2 plasticization pressure of 300 psi.