Several strategies have been used to increase the biostability of medical-grade polyurethanes while maintaining biocompatibility and mechanical properties. One approach is to chemically modify or replace the susceptible soft segment. Currently, poly(carbonate urethanes) (PCUs) are being evaluated as a replacement of poly(ether urethanes) (PEUs) in medical devices because of the increased oxidative stability of the polycarbonate soft segment. Preliminary in vivo and in vitro studies have reported improved biostability of PCUs over PEUs. Although several studies have reported evidence of in vitro degradation of these new polyurethanes, there has been no evidence of significant in vivo degradation that validates a degradation mechanism. In this study, the effect of soft segment chemistry on the phase morphology, mechanical properties, and in vivo response of commercial-grade PEU and PCU elastomers was examined. Results from dynamic mechanical testing and infrared spectroscopy suggested that the phase separation was better in PCU as compared with PEU. In addition, the higher modulus and reduced ultimate elongation of PCU was attributed to the reduced flexibility of the polycarbonate soft segment. Following material characterization, the in vivo biostability and biocompatibility of PEU and PCU were studied using a subcutaneous cage implant protocol. The results from the cage implant study and cell culture experiments indicated that monocytes adhere, differentiate, and fuse to form foreign body giant cells on both polyurethanes. It is now generally accepted that the reactive oxygen species released by these adherent macrophages and foreign body giant cells initiate PEU biodegradation. Attenuated total reflectance-Fourier transform infrared analysis of explanted samples provided evidence of chain scission and crosslinking in both polyurethanes. This indicated that the PCU was also susceptible to biodegradation by agents released from adherent cells. These results reinforce the need to evaluate and understand the biodegradation mechanisms of PCUs.
Autologous nerve grafts are currently the best option for the treatment of segmental peripheral nerve defects. However, autografts have several drawbacks including size mismatch and loss of sensation in the donor nerve's sensory distribution. In this work, we have investigated the development of a synthetic hydrogel that contains positive charge for use as a substrate for nerve cell attachment and neurite outgrowth in culture. We have demonstrated that modification of oligo-(polyethylene glycol) fumarate (OPF) with a positively charged monomer improves primary sensory rat neuron attachment and differentiation in a dose-dependent manner. Positively charged hydrogels also supported attachment of dorsal root ganglion (DRG) explants that contain sensory neurons, Schwann cells and neuronal support cells. Furthermore, charged hydrogels were analyzed for the appearance of myelinated structures in a co-culture containing DRG neurons and Schwann cells. DRGs and Schwann cells remained viable on charged hydrogels for a time period of three weeks and neurites extended from the DRGs. Sudan black staining revealed that neurites emerging from DRGs were accompanied by migrating Schwann cells. These findings suggest that charged OPF hydrogels are capable of sustaining both primary nerve cells and the neural support cells that are critical for regeneration.
This study describes investigation of porous photocrosslinked oligo[(polyethylene glycol) fumarate] (OPF) hydrogels as potential matrix for osteoblastic differentiation of marrow stromal cells (MSCs). The porosity and interconnectivity of porous hydrogels were assessed using magnetic resonance microscopy (MRM) as a noninvasive investigative tool that could image the water construct inside the hydrogels at a high-spatial resolution. MSCs were cultured onto the porous hydrogels and cell number was assessed using PicoGreen DNA assay. Our results showed 10% of cells initially attached to the surface of scaffolds. However, cells did not show significant proliferation over a time period of 14 days. MSCs cultured on porous hydrogels had increased alkaline phosphatase activity as well as deposition of calcium, suggesting successful differentiation and maturation to the osteoblastic phenotype. Moreover, continued expression of type I collagen and osteonectin over 14 days confirmed osteoblastic differentiation of MSCs. MRM was also applied to monitor osteogenesis of MSCs on porous hydrogels. MRM images showed porous scaffolds became consolidated with osteogenic progression of cell differentiation. These findings indicate that porous OPF scaffolds enhanced MSC differentiation leading to development of bone-like mineralized tissue.
Histone deacetylase 3 (Hdac3) is a nuclear enzyme that removes acetyl groups from lysine residues in histones and other proteins to epigenetically regulate gene expression. Hdac3 interacts with bone-related transcription factors and co-factors such as Runx2 and Zfp521, and thus is poised to play a key role in the skeletal system. To understand the role of Hdac3 in osteoblasts and osteocytes, Hdac3 conditional knockout (CKO) mice were created with the Osteocalcin (OCN) promoter driving Cre expression. Hdac3 CKOOCN mice were of normal size and weight, but progressively lost trabecular and cortical bone mass with age. The Hdac3 CKOOCN mice exhibited reduced cortical bone mineralization and material properties and suffered frequent fractures. Bone resorption was lower, not higher, in the Hdac3 CKOOCN mice, suggesting that primary defects in osteoblasts caused the reduced bone mass. Indeed, reductions in bone formation were observed. Osteoblasts and osteocytes from Hdac3 CKOOCN mice showed increased DNA damage and reduced functional activity in vivo and in vitro. Thus, Hdac3 expression in osteoblasts and osteocytes is essential for bone maintenance during aging.
Electrically conductive hydrogel composites consisting of oligo(polyethylene glycol) fumarate (OPF) and polypyrrole (PPy) were developed for applications in nerve regeneration. OPF-PPy scaffolds were synthesized using three different anions: naphthalene-2-sulfonic acid sodium salt (NSA), dodecylbenzenesulfonic acid sodium salt (DBSA), and dioctyl sulfosuccinate sodium salt (DOSS). Scaffolds were characterized by ATR-FTIR, XPS, AFM, dynamic mechanical analysis, electrical resistivity measurements, and swelling experiments. OPF-PPy scaffolds were shown to consist of up to 25 mol% polypyrrole with a compressive modulus ranging from 265 to 323 kPa and a sheet resistance ranging from 6 to 30 × 103 Ohms/square. In vitro studies using PC12 cells showed OPF-PPy materials had no cytotoxicity and PC12 cells showed distinctly better cell attachment and an increase in the percent of neurite bearing cells on OPF-PPy materials compared to OPF. The neurite lengths of PC12 cells were significantly higher on OPF-PPyNSA and OPF-PPyDBSA. These results show that electrically conductive OPF-PPy hydrogels are promising candidates for future applications in nerve regeneration.
Photo-cross-linkable oligo[poly(ethylene glycol) fumarate] (OPF) hydrogels have been developed for use in tissue engineering applications. We demonstrated that compressive modulus of these hydrogels increased with increasing polymer concentration, and hydrogels with different mechanical properties were formed by altering the ratio of cross-linker/polymer in precursor solution. Conversely, swelling of hydrogels decreased with increasing polymer concentration and cross-linker/polymer ratio. These hydrogels are degradable and degradation rates vary with the change in cross-linking level. Chondrocyte attachment was quantified as a method for evaluating adhesion of cells to the hydrogels. These data revealed that cross-linking density affects cell behavior on the hydrogel surfaces. Cell attachment was greater on the samples with increased cross-linking density. Chondrocytes on these samples exhibited spread morphology with distinct actin stress fibers, whereas they maintained their rounded morphology on the samples with lower cross-linking density. Moreover, chondrocytes were photoencapsulated within various hydrogel networks. Our results revealed that cells encapsulated within 2-mm thick OPF hydrogel disks remained viable throughout the 3-week culture period, with no difference in viability across the thickness of hydrogels. Photoencapsulated chondrocytes expressed the mRNA of type II collagen and produced cartilaginous matrix within the hydrogel constructs after three weeks. These findings suggest that photo-cross-linkable OPF hydrogels may be useful for cartilage tissue engineering and cell delivery applications.
The transected rat thoracic (T9/10) spinal cord model is a platform for quantitatively compa0ring biodegradable polymer scaffolds. Schwann cell-loaded scaffolds constructed from poly (lactic co-glycolic acid) (PLGA), poly(ε-caprolactone fumarate) (PCLF), oligo(polyethylene glycol) fumarate (OPF) hydrogel or positively charged OPF (OPF+) hydrogel were implanted into the model. We demonstrated that the mechanical properties (3-point bending and stiffness) of OPF and OPF+ hydrogels closely resembled rat spinal cord. After one month, tissues were harvested and analyzed by morphometry of neurofilament-stained sections at rostral, midlevel, and caudal scaffold. All polymers supported axonal growth. Significantly higher numbers of axons were found in PCLF (P < 0.01) and OPF+ (P < 0.05) groups, compared to that of the PLGA group. OPF+ polymers showed more centrally distributed axonal regeneration within the channels while other polymers (PLGA, PCLF and OPF) tended to show more evenly dispersed axons within the channels. The centralized distribution was associated with significantly more axons regenerating (P < 0.05). Volume of scar and cyst rostral and caudal to the implanted scaffold was measured and compared. There were significantly smaller cyst volumes in PLGA compared to PCLF groups. The model provides a quantitative basis for assessing individual and combined tissue engineering strategies.
We present enhanced cell ingrowth and proliferation through crosslinked three-dimensional (3D) nanocomposite scaffolds fabricated using poly(propylene fumarate) (PPF) and hydroxyapatite (HA) nanoparticles. Scaffolds with controlled internal pore structures were produced from computer-aided design (CAD) models and solid freeform fabrication (SFF) technique, while those with random pore structures were fabricated by NaCl leaching technique for comparison. The morphology and mechanical properties of scaffolds were characterized using scanning electron microscopy (SEM) and mechanical testing, respectively. Pore interconnectivity of scaffolds was assessed using X-ray micro-computed tomography (micro-CT) and 3D imaging analysis. In vitro cell studies have been performed using MC3T3-E1 mouse preosteoblasts and cultured scaffolds in a rotating-wall-vessel bioreactor for 4 and 7 days to assess cell attachment, viability, ingrowth depth, and proliferation. The mechanical properties of crosslinked nanocomposite scaffolds were not significantly different after adding HA or varying pore structures. However, pore interconnectivity of PPF/HA nanocomposite scaffolds with controlled pore structures has been significantly increased, resulting in enhanced cell ingrowth depth 7 days after cell seeding. Cell attachment and proliferation are also higher in PPF/ HA nanocomposite scaffolds. These results suggest that crosslinked PPF/HA nanocomposite scaffolds with controlled pore structures may lead to promising bone tissue engineering scaffolds with excellent cell proliferation and ingrowth.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.