Stability of quantum dot (QD) films is an issue of concern for applications in devices such as solar cells, LEDs, and transistors. This paper analyzes and optimizes the passivation of such QD films using gas-phase deposition, resulting in enhanced stability. Crucially, we deposited alumina at economically attractive conditions, room temperature and atmospheric pressure, on (1,2-ethanediamine) capped PbSe QD films using an approach based on atomic layer deposition (ALD), with trimethylaluminum (TMA) and water as precursors. We performed coating experiments from 1 to 25 cycles on the QD films, finding that alumina formed from the first exposure of TMA. X-ray photoelectron spectroscopy points to the presence of oxygen-rich compounds on the bare QD films, most likely from entrapped solvent molecules during the assembly of the QD films. These oxygenated compounds and the amine groups of the organic ligands react with TMA in the first cycle, resulting in a fast growth of alumina. Using 10 cycles resulted in a QD film that was optically stable for at least 27 days. Depositing alumina at ambient conditions is preferred, since the production of the QD films is also carried out at room temperature and atmospheric pressure, allowing combination of both processes in a single go.

MoS2 supported on oxides like TiO2 has a broad range of applications. The atomic structure of this system is therefore very useful to study. Previous research work in this area has made use of high-temperature synthesis methods, while the preparation of an MoS2/TiO2 in very important applications, such as catalysis, makes use of a low-temperature synthesis method. In this work, we investigate a low-temperature synthesis strategy for MoS2 slabs supported on rutile TiO2(110). Using scanning tunneling microscopy and X-ray photoelectron spectroscopy, we demonstrate that not only flat MoS2 slabs with irregular shapes but also MoSx stripes with a large number of coordinatively unsaturated Mo atoms are formed. In particular, it becomes evident that, for atomic structural characterization of MoS2/TiO2 and similar oxide-supported systems grown by low-temperature synthesis methods, the surface structure of the support becomes highly relevant.

Transition metal dichalcogenides (TMDCs) are a type of two-dimensional (2D) material that has been widely investigated by both experimentalists and theoreticians because of their unique properties. In the case of cobalt sulfide, density functional theory (DFT) calculations on free-standing S–Co–S sheets suggest there are no stable 2D cobalt sulfide polymorphs, whereas experimental observations clearly show TMDC-like structures on Au(111). In this study, we resolve this disagreement by using a combination of experimental techniques and DFT calculations, considering the substrate explicitly. We find a 2D CoS(0001)-like sheet on Au(111) that delivers excellent agreement between theory and experiment. Uniquely this sheet exhibits a metallic character, contrary to most TMDCs, and exists due to the stabilizing interactions with the Au(111) substrate.

Here we present the results of a study carried out to investigate the simultaneous sulfidation of Co and Mo oxide nanoparticles on Au(111) as a synthesis strategy to prepare a...

No abstract