In this research, surface modification of aromatic polyamide thin film composite (TFC) reverse osmosis (RO) membranes was carried out using dielectric barrier discharge (DBD) plasma treatment to improve the performance and fouling resistance of prepared RO membranes. First, polyamide TFC RO membranes were synthesized via interfacial polymerization of m‐phenylenediamine and trimesoyl chloride monomers over microporous polysulfone support membrane. Next, the DBD plasma treatment with 15 s, 30 s, 60 s, and 90 s duration was used for surface modification. The surface properties of RO membranes were characterized by attenuated total reflectance Fourier transform infrared spectroscopy (ATR‐FTIR), SEM, AFM, and contact angle measurements. The ATR‐FTIR results indicated that DBD plasma treatment caused hydrogen bonding on the surface of RO membranes. Also, the contact angle measurement showed that the hydrophilicity of the membranes was increased due to DBD plasma treatment. The changes in the membranes surface morphology indicated that the surface roughness of the membranes was increased after surface modification. In addition, it was found that the DBD plasma treatment increased the water permeation flux significantly and enhanced sodium chloride (NaCl) salt rejection slightly. Moreover, the filtration of bovine serum albumin revealed that the antifouling properties of the modified membranes had been improved. POLYM. ENG. SCI., 59:E468–E475, 2019. © 2018 Society of Plastics Engineers

No abstract

The purpose of this research is to explain the surface modification of fabricated polyamide reverse osmosis (RO) membranes using UV-initiated graft polymerization at different irradiation times (15, 30, 60, and 90 s) and various acrylamide concentrations (10, 20, and 30 g L −1 ). Also, coating of membranes surface with various concentrations of TiO 2 nanoparticles (10, 20, 30, and 50 ppm) followed by the same UV irradiation times was investigated. After that, the membranes modification was done by grafting of acrylamide blended with TiO 2 nanoparticles via UV irradiation. The characterization of membranes surface properties and their performance were systematically carried out. The results demonstrated the enhanced hydrophilicity of modified membranes and confirmed the presence of acrylamide and nanoparticles on the membranes surface. Acrylamide-grafted membranes could reach to higher water flux than pristine membrane with little reduction in salt rejection. Moreover, TiO 2 -coated membranes indicated enhancement of water flux continuously with increase in nanoparticles concentration and irradiation time and rejection of membranes was slightly decreased at low irradiation times. Also, RO membranes modified simultaneously with acrylamide and TiO 2 nanoparticles under UV irradiation exhibited improved water flux up to 18%, slightly higher rejection, and considerable better fouling resistance compared with pristine one.