The heat‐affected zone (HAZ) softening is considered one of the most significant challenges during welding of ferrite–martensite dual‐phase (DP) steels. In fact, the strain localization in the softened area results in a premature fracture that degrades the mechanical properties of the joint. Herein, the objective is to investigate the effectiveness of improved cooling using a high thermal diffusivity backing plate (BP) to reduce HAZ softening and enhance the mechanical properties of friction stir‐welded DP700 steel. Accordingly, friction stir butt welding of DP700 steel was conducted using copper and mild steel BPs. The findings show that the replacement of steel BP with copper significantly reduces the weld temperature. It is also observed that the thermal diffusivity of the BP has a substantial effect on the microstructure development and mechanical properties of the welded joint. Increasing the thermal diffusivity of the BP results in a reduction of HAZ softening from 20 to 7 HV and improving tensile strength and total elongation of the joint by 40 MPa and 6.2%, respectively. Work hardening behavior and absorbed energy before the fracture are significantly improved by the replacement of steel BP with a copper.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.