Herein, the NH2-UiO-66 metal organic framework (MOF) has been green synthesized with the assistance of high gravity to provide a suitable and safe platform for drug loading. The NH2-UiO-66 MOF was characterized using a field-emission scanning electron microscope, transmission electron microscope (TEM), X-ray diffraction, and zeta potential analysis. Doxorubicin was then encapsulated physically on the porosity of the green MOF. Two different stimulus polymers, p­(HEMA) and p­(NIPAM), were used as the coating agents of the MOFs. Doxorubicin was loaded onto the polymer-coated MOFs as well, and a drug payload of more than 51% was obtained, which is a record by itself. In the next step, pCRISPR was successfully tagged on the surface of the modified MOFs, and the performance of the final nanosystems were evaluated by the GFP expression. In addition, successful loadings and internalizations of doxorubicin were investigated via confocal laser scanning microscopy. Cellular images from the HeLa cell line for the UiO-66@DOX@pCRISPR and GMA-UiO-66@DOX@pCRISPR do not show any promising and successful gene transfections, with a maximum EGFP of 1.6%; however, the results for the p­(HEMA)-GMA-UiO-66@DOX@pCRISPR show up to 4.3% transfection efficiency. Also, the results for the p­(NIPAM)-GMA-UiO-66@DOX@pCRISPR showed up to 6.4% transfection efficiency, which is the first and superior report of a MOF-based nanocarrier for the delivery of pCRISPR. Furthermore, the MTT assay does not shown any critical cytotoxicity, which is a promising result for further biomedical applications. At the end of the study, the morphologies of all of the nanomaterials were screened after drug and gene delivery procedures and showed partial degradation of the nanomaterial. However, the cubic structure of the MOFs has been shown in TEM, and this is further proof of the stability of these green MOFs for biomedical applications.

No abstract

No abstract

The magnetic MOF-based catalytic system has been reported here to be an efficient catalyst for synthesis of benzonitriles and diarylethers of aryl halides under optimal conditions. The MOF catalyst was built based on magnetic nanoparticles and UiO-66-NH2 which further modified with 2,4,6-trichloro-1,3,5-triazine and 5-phenyl tetrazole at the same time and the catalyst structure was confirmed by various techniques. This new modification has been applied to increase anchoring palladium into the support. Furthermore, the products’ yields were obtained in good to excellent for all reactions under mild conditions which result from superior activity of the synthesized heterogeneous catalyst containing palladium. Also, the magnetic property of the MOF-based catalyst makes it easy to separate from reaction mediums and reuse in the next runs.

The postsynthetic modification of metal–organic frameworks (MOFs) has opened up a promising area to widen their water treatment application. However, their polycrystalline powdery state still restricts their widespread industrial-scale applications. Herein, the magnetization of UiO-66-NH2 is reported as a promising approach to facilitate the separation of the used MOFs after water treatment. A two-step postmodification procedure employing 2,4,6-trichloro-1,3,5-triazine (TCT) and 5-phenyl-1H-tetrazole (PTZ) agents was introduced to level up the adsorption performance of the magnetic nanocomposite. Despite a decrement in porosity and specific surface area of the designed MOFs (m-UiO-66-TCT) compared to neat UiO-66-NH2, it outweighs in adsorption capacity. It was observed that m-UiO-66-TCT has an adsorption capacity of ≈298 mg/g for methyl orange (MO) with facile MOF separation using an external magnet. Pseudo-second-order kinetic model and Freundlich isotherm models suitably interpret the experimental data. Thermodynamic studies showed that MO removal using m-UiO-66-TCT is spontaneous and thermodynamically favorable at higher temperatures. The m-UiO-66-TCT composite exhibited easy separation, high adsorption capacity, and good recyclability, rendering it an attractive candidate for the adsorptive removal of MO dye from aqueous environments.