The bonding strength, mechanical properties and high-temperature thermal shock resistance of C/C-SiC composites after undergoing simulated low earth orbit environment including cryogenic thermal cycles (CTCs) between 153 and 393 K for 200 times with high-vacuum state of 1.3 × 10 −3 Pa were investigated. Results of the tests showed that, the bonding strength at coating/substrate interface monotonically decreased as the CTCs increased. After 100 CTCs, the flexural strength of C/C-SiC composites enhanced and the percentage of remaining strength was 102.60%, while, the mass loss of specimens decreased from 2.08 to 0.89% after thermal shock resistance test between 1773 K and room temperature for 15 times. Once CTCs exceed 100 times, the mass loss increased, the flexural strength reduced and remained only 87.40% of initial strength after 200 CTCs. The fractural behaviour of CTCs-treated modified composites exhibited typical brittle mode. A model based on the evolution of the residual thermal stress after CTCs treatment was proposed to explain the oxidation failure mechanism of C/C-SiC specimens.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.