Background: Hospital equipment made from copper alloys can play an important role in complementing traditional methods of disinfection. Aims of the study: The aim of this study was to assess the dynamics of the antimicrobial properties of selected copper alloys in different simulations of environmental conditions (with organic contamination vs. without organic contamination), and to test alternatives to the currently used testing methods. Materials and Methods: A modification of Japanese standard JIS Z 2801 as well as Staphylococcus aureus (SA) and Escherichia coli (EC) suspended in NaCl vs. tryptic soy broth (TSB) were used in tests performed on seven commonly used copper alloys, copper, and stainless steel. Results: A much faster reduction of the bacterial suspension was observed for the inoculum prepared in NaCl than in TSB. A faster reduction for EC than for SA was observed in the inoculum prepared in NaCl. The opposite results were found for the inoculum based on TSB. A significant correlation between the copper concentration in the copper alloys and the time and degree of bacterial suspension reduction was only observed in the case of EC. Conclusions: This study confirmed the antimicrobial properties of copper alloys, and additionally showed that Staphylococcus aureus was more resistant than Escherichia coli in the variant of the experiment without organic contamination. However, even for SA, a total reduction of the bacterial inoculum’s density took no longer than 2 h. Under conditions simulating organic contamination, all of the tested alloys were shown to have bactericidal or bacteriostatic properties, which was contrary to the results from stainless steel.
BackgroundDespite the employment of sanitary regimes, contact transmission of the aetiological agents of hospital infections is still exceedingly common. The issue of microbe transmission becomes particularly important when facing multidrug-resistant microorganisms such as methicillin-resistant staphylococci. In the case of deficiencies in cleaning and disinfection procedures, hospital equipment made of copper alloys can play an important role, complementing traditional hospital hygiene procedures.The objective of this study was to characterize staphylococcal strains isolated from touch surfaces in Polish hospital wards in terms of their drug resistance, ability to form biofilm and susceptibility to antimicrobial activity of copper alloys.MethodsThe materials for the study were 95 staphylococcal strains isolated from touch surfaces in 13 different hospital wards from Małopolska province (the south of Poland). Phenotypic and genotypic antibiotic resistance were checked for erythromycin, clindamycin, gentamycin, ciprofloxacin, trimethoprim/sulfamethoxazole and mupirocin. Biofilm formation ability for the tested strains was checked with the use of culture on Congo red agar. Susceptibility to copper, tin bronze, brass and new silver was tested using a modification of the Japanese standard.ResultsOver 67% of the analysed staphylococcal strains were methicillin-resistant (MR). Four strains were resistant to all of the tested antibiotics, and 14 were resistant to all except mupirocin. Strains classified as MR had significantly increased resistance to the remaining antibiotic groups. About one-third of the analysed strains revealed biofilm-forming ability. Among the majority of species, biofilm-forming and non-biofilm-forming strains were distributed evenly; in the case of S. haemolyticus only, negative strains accounted for 92.8%. Susceptibility to copper alloys was different between strains and rather lower than in the case of the SA strain selected for comparison.ConclusionsCoagulase-negative staphylococci, the most commonly isolated in Polish hospital wards, should not be neglected as an infection risk factor due their high antibiotic resistance. Our experiments confirmed that touch surfaces made of copper alloys may play an important role in eliminating bacteria from the hospital environment.
Al-Mg-Si alloys are used not only as construction material, but also as a material for electrical conductors. For this application, it is crucial for the alloy to achieve a balance between strength and electrical properties. This is achieved in practice by a combination of strain and precipitation hardening. The current paper focuses on a heat treatment procedure in which the EN AW 6101 alloy is cooled by a flowing air stream from the solutionizing temperature down to the artificial ageing temperature. The proposed procedure, unlike the common heat treatment leading to the T6 temper, allowed for the precipitation of the coarser β” phase with the presence of relatively wide precipitate-free zones. The age hardening response was investigated by Brinell hardness measurements, eddy current testing and microstructural observations using transmission electron microscopy (TEM). The applied heat treatment resulted in slightly lower strength (compared to the T6 temper), but improved electrical performance of the alloy.
Due to specific application of the Zn-Cu-Ti alloy rolled sheets as a roofing material, ready-made sheets has to meet some specific requirements of bendability at relatively low temperatures, as low as 5°C. In the current paper it was shown that susceptibility of the Zn-Cu-Ti sheets to low temperature bending, is closely related to degree of its dynamic recrystallization during rolling process. The paper discusses effect of different technological routes on the microstructure, mechanical properties and in particular the low temperature performance of Zn-Cu-Ti rolled sheets. The experimental results shows that the homogenization of Zn-Cu-Ti casted strips at the pre-rolling stage can play important role in recrystallization of the sheets during rolling. The current work is part of research on designing new technological route.
Among multiple applications 6XXX-series aluminum alloys are widely used as electrical conductor for overhead power lines. For that application Al-Mg-Si alloys are produced mainly in the form of wire rod in the continuous casting and rolling lines (CCR). There is many technological routes possible to transform the Al-Mg-Si wire-rod into precipitation hardened, ready to use Al-Mg-Si wires. One of these routes involves using the heat of continuous casting and rolling process to artificial ageing of wire-rod, which is motivated by ecological premise. In the current paper the results of continuous heat treatment of the wire-rod within the CCR line (involving quenching of the alloy to artificial ageing temperature) on the microstructure and properties has been examined. It was shown the structure of wire rod formed in such process is very irregular. TEM investigations has shown that many heterogeneous particles are present and the arrangement of the β main hardening phase is very inhomogeneous with wide precipitate free zones occurred. However this type of microstructure has a positive effect on electrical properties of the material in question, which is important taking into consideration application of the alloy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.