We present an optical spectroscopy study of Cu 2 ZnSnSe 4 (CZTSe) thin films deposited on Mo/glass substrates. The [Cu]/[Zn+Sn] ratio in these films varies from nearly stoichiometric to strongly Cu deficient and Zn rich. Increasing Cu deficiency and Zn excess widens the bandgap E g , determined using photoluminescence excitation (PLE) at 4.2 K, from 0.99 eV to 1.03 eV and blue shifts the dominant band in the photoluminescence (PL) spectra from 0.83 eV to 0.95 eV. The PL spectra of the near stoichiometric film reveal two bands: a dominant band centred at 0.83 eV and a lower intensity one at 0.93 eV. The temperature and excitation intensity dependence of the PL spectra help to identify the recombination mechanisms of the observed emission bands as free-to-bound: recombination of free electrons with holes localised at acceptors affected by randomly distributed potential fluctuations. Both the mean 2 depth of such fluctuations, determined by analysing the shape of the dominant bands, and the broadening energy, estimated from the PLE spectra, become smaller with increasing Cu deficiency and Zn excess which also widens E g due to an improved ordering of the Cu/Zn atoms. These changes in the elemental composition induce a significant blue shift of the PL bands exceeding the E g widening. This is attributed to a change of the dominant acceptor for a shallow one, and is beneficial for the solar cell performance. Film regions with a higher degree of Cu/Zn ordering are present in the near stoichiometric film generating the second PL band at 0.93 eV.

We present structural and optical spectroscopy studies of thin films of Cu2ZnSnSe4 (CZTSe) with strong copper deficiency deposited on Mo/Glass substrates and selenised at 450, 500 or 550 °C. Solar cells fabricated from these films demonstrated efficiencies up to 7.4% for selenisation at 500 °C. Structural analysis based on X-ray diffraction and Raman spectroscopy revealed the presence of SnSe2 in the film selenised at 450 °C but not detected in the films selenised at higher temperatures. A progressive decrease of the Sn and Se content was observed as the selenisation temperature increased. Photoluminescence excitation was used to determine the bandgaps at 4.2 K. Detailed measurements of the temperature and excitation intensity dependencies of the photoluminescence spectra allow the recombination mechanisms of the observed emission bands to be identified as band-to-impurity and band-to-band transitions, and their evolution with selenisation temperature changes to be analysed. The strongest band-to-band transition is recorded in the PL spectra of the film selenised at 500 °C and can be observed from 6 K to room temperature. The compositional and structural changes in the films and their influence on the optoelectronic properties of CZTSe and solar cells are discussed