Amorphous hydrogenated Si 1-x C x / SiC multilayers consisting of alternating Si 1-x C x and stoichiometric SiC layers were prepared using Plasma Enhanced Chemical Vapour Deposition (PECVD). Annealing at temperatures up to 1100°C was done targeting the size controlled crystallization of Si nanocrystals (NCs) in a SiC matrix. The influence of annealing temperature on the nanostructure of the multilayers was studied using Glancing Incidence X-ray Diffraction (GIXRD), Raman spectroscopy and Transmission Electron Microscopy (TEM). GIXRD reveal the crystallization of Si and SiC, when annealing temperatures exceed 900°C. The crystallization of Si and SiC was confirmed by TEM bright field imaging and electron diffraction. Annealing at 900°C, leads to the formation of Si NCs with a size of 3 nm, whereas the SiC NCs also have a size of 3 nm. However, a large amount of Si is still amorphous as shown by Raman spectroscopy. Annealing at temperatures exceeding 900°C reduces the amorphous phase and a further growth of Si NCs occurs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.