The aim of this research is to study the role of nanocrystalline TiO2/SnO2 n–n heterojunctions for hydrogen sensing. Nanopowders of pure SnO2, 90 mol % SnO2/10 mol % TiO2, 10 mol % SnO2/90 mol % TiO2 and pure TiO2 have been obtained using flame spray synthesis (FSS). The samples have been characterized by BET, XRD, SEM, HR-TEM, Mössbauer effect and impedance spectroscopy. Gas-sensing experiments have been performed for H2 concentrations of 1–3000 ppm at 200–400 °C. The nanomaterials are well-crystallized, anatase TiO2, rutile TiO2 and cassiterite SnO2 polymorphic forms are present depending on the chemical composition of the powders. The crystallite sizes from XRD peak analysis are within the range of 3–27 nm. Tin exhibits only the oxidation state 4+. The H2 detection threshold for the studied TiO2/SnO2 heterostructures is lower than 1 ppm especially in the case of SnO2-rich samples. The recovery time of SnO2-based heterostructures, despite their large responses over the whole measuring range, is much longer than that of TiO2-rich samples at higher H2 flows. TiO2/SnO2 heterostructures can be intentionally modified for the improved H2 detection within both the small (1–50 ppm) and the large (50–3000 ppm) concentration range. The temperature T
max at which the semiconducting behavior begins to prevail upon water desorption/oxygen adsorption depends on the TiO2/SnO2 composition. The electrical resistance of sensing materials exhibits a power-law dependence on the H2 partial pressure. This allows us to draw a conclusion about the first step in the gas sensing mechanism related to the adsorption of oxygen ions at the surface of nanomaterials.
TiO2-based nanopowders are elaborated by flame spray synthesis, FSS from organic precursors of titanium and chromium with the Cr content changing from 0 to 15 at.%. Well-crystallized nanopowders with high specific surface area SSA reaching 107 m2/g for undoped TiO2 and 177 m2/g for TiO2 + 15 at.% Cr are obtained. Thin films are deposited by rf reactive sputtering from metallic Ti and Ti-Cr targets in Ar + O2 flow controlled atmosphere. The adjustable area of Cr/Ti allows to obtain up to 16 at.% Cr in TiO2 thin films. X-ray diffraction, transmission electron spectroscopy, TEM, atomic force microscopy, AFM and optical spectrophotometry over the ultraviolet UV and visible VIS range of the light spectrum have been performed in order to characterize the nanomaterials. The particle size of nanopowders is within the range of 5-42 nm. Anatase is the predominating polymorphic form while the amount of rutile increases with Cr content to reach of about 25 wt.% at 15 at.% Cr. The post-deposition annealing of thin films in air at temperatures from 770 K to 1280 K modifies the phase composition, leads to irreversible transformation from anatase to rutile and affects the surface roughness. Structural and optical properties of TiO2-based nanopowders and thin films are compared. The effect of grain size and the level of chromium doping on the band gap E(g) is discussed. Photocatalytic activity of the nanopowders is tested for degradation of methylene blue, MB.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.