raj (2017) Synthesis of the semi-organic nonlinear optical crystal l-glutamic acid zinc chloride and investigation of its growth and physiochemical properties,
A novel semiorganic nonlinear optical (NLO) crystal, bis(thiourea) barium nitrate (BTBN) was synthesized and grown by slow evaporation method. Structure of the new crystalline compound was confirmed by single crystal X-ray diffraction analysis and it showed that BTBN belongs to orthorhombic crystal system. The crystalline nature of the BTBN was confirmed by powder X-ray diffraction study. Important functional groups of BTBN were identified by FT-IR spectroscopic analysis. UV-Vis-NIR spectral study showed that the grown crystal is transparent in the entire visible region with low cut off wavelength of 304 nm. BTBN exhibits a SHG efficiency which is nearly 2.38 times higher than that of KDP. The BTBN crystal has high mechanical strength and belongs to soft category, which was confirmed by micorhardness study. The thermal stability of BTBN was determined from TGA and DTA thermal study which revealed that the BTBN crystal has thermal stability up to 243.1 °C. The surface properties and presence of elements was analyzed by SEM and EDAX study, respectively.
Please cite this article in press as: M. Packiya raj, et al. Synthesis, growth, and structural, optical, mechanical, electrical properties of a new inorganic nonlinear optical crystal: Sodium manganese tetrachloride (SMTC), J. Taibah Univ. Sci. (2015), http://dx.
AbstractA new inorganic nonlinear optical single crystal of sodium manganese tetrachloride (SMTC) has been successfully grown from aqueous solution using the slow evaporation technique at room temperature. The crystals obtained using the aforementioned method were characterized using different techniques. The crystalline nature of the as-grown crystal of SMTC was analyzed using powder X-ray diffraction. Single-crystal X-ray diffraction revealed that the crystal belongs to an orthorhombic system with noncentrosymmetric space group Pbam. The optical transmission study of the SMTC crystal revealed high transmittance in the entire UV-vis region, and the lower cut-off wavelength was determined to be 240 nm. The mechanical strength of the as-grown crystal was estimated using the Vickers microhardness test. The second harmonic generation (SHG) efficiency of the crystal was measured using Kurtz's powder technique, which indicated that the crystal has a nonlinear optical (NLO) efficiency that is 1.32 times greater than that of KDP. The dielectric constant and dielectric loss of the compound were measured at different temperatures with varying frequencies. The photoconductivity study confirmed that the title compound possesses a negative photoconducting nature. The growth mechanism and surface features of the as-grown crystals were investigated using chemical etching analysis.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.