Phase equilibria in the Co-Fe-La system were studied using differential thermal analysis (DTA), X-ray diffraction analysis, scanning electron microscopy (SEM), and electron probe microanalysis (EPMA). Liquidus and solidus projections and a melting diagram for this system over the whole concentration range and a Scheil diagram for solidification were constructed. The ternary compound (Co,Fe) 17 La 2 (s) (Th 2 Zn 17 -type structure) forms by peritectic reaction L ? (cCo,Fe) ? Co 13 La ¢ s at 978°C. This ternary compound is located along the isoconcentrate of 11 at.% La and extends from 45.8 to 79.3 at.% Co. The Co 13 La phase has the widest homogeneity region and dissolves up to 43.3 at.% Fe. The solubilities of Fe in Co 5 La, Co 7 La 2 , Co 19 La 5 , and Co 3 La 2 were established to be 10.3, 9.2, 4.7, and 3.2 at.%, respectively. The solubility of Fe in Co 1.7 La 2 and CoLa 3 according to EPMA does not exceed 1 at.%. The maximum solubility of La in (cCo,Fe) and (aCo,Fe) is determined to be less than 1 at.%.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.