We report on optically pumped lasing at 500 nm on InGaN laser structures grown by plasma assisted molecular beam epitaxy. The InGaN laser structures were grown under group III-rich conditions on bulk (0001) GaN substrates. The influence of the nitrogen flux and growth temperature on the indium content of InGaN layers was studied. We demonstrate that at elevated growth temperatures, where appreciable dissociation rate for In-N bonds is observed, the indium content of InGaN layers increases with increasing nitrogen flux. We show that growth of InGaN at higher temperatures improves optical quality of InGaN quantum wells, which is crucial for green emitters. The influence of piezoelectric fields on the lasing wavelength is also discussed. In particular, the controversial issue of partial versus complete screening of built-in electric field at lasing conditions is examined, supporting the former case.
The growth of N-polar (In,Ga)N structures by plasma-assisted molecular beam epitaxy is studied. (In,Ga)N multiple quantum well samples with atomically smooth surface were grown and their good structural quality was confirmed by x-ray diffraction, scanning transmission electron microscopy, and defect selective etching. The In incorporation was higher in the N-polar than in the Ga-polar oriented crystal, consistent with previous reports. However, despite the good morphological and structural properties of these samples, no photoluminescence signal from the (In,Ga)N wells was detected. In contrast, a thick N-polar (In,Ga)N layer exhibited a broad peak at 620 nm in good agreement with the In content determined by x-ray diffraction. The potential source of the luminescence quenching in the N-polar (In,Ga)N multiple quantum wells is discussed and attributed either to a strong nonradiative recombination channel at the surface promoted by the electric field or to the high concentration of point defects at the interfaces of the quantum well structures.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.