In this study, catalytic and noncatalytic pyrolysis of Prosopis juliflora biomass was carried out in a fluidized bed reactor. This study highlights the potential use of forestry residues with waste eggshells under a nitrogen environment. The experiments were conducted to increase the yield of bio-oil by changing the parameters such as pyrolysis temperature, particle size, and catalyst ratio. Under noncatalytic pyrolysis, a maximum bio-oil yield of 40.9 wt% was obtained when the feedstock was pyrolysed at 500°C. During catalytic pyrolysis, the yield of bio-oil was increased by up to 16.95% compared to the noncatalytic process due to the influence of Ca-rich wastes on devolatilization behavior. In particular, the existence of alkali and alkaline-earth metals present in eggshells might have positive effects on the decomposition of biomass material. The bio-oil obtained through catalytic pyrolysis under maximum yield conditions was analyzed for its physical and chemical characterization by Fourier transform infrared (FT-IR) spectroscopy and gas chromatography mass spectroscopy (GC-MS).

The enhancement of composites’ mechanical characteristics (tensile, compressive, and hardness) is a constant demand for technological advancement. The stir casting process is used to make the hybrid aluminium alloy metal matrix composites Al 6061-SiC-AlN in our present study. To create mechanical qualities such as tensile, compressive, and hardness, silicon carbide and aluminium nitride (both 3% and 6%) were utilized as the reinforcement. The tensile strength, compressive strength, and hardness of the Al 6061-SiC-AlN hybrid composites samples were determined. The tensile, compressive, and hardness parameters of Al 6061-SiC-AlN hybrid composites are estimated and evaluated to those of the matrix Al 6061 alloy. With the inclusion of silicon carbide and AlN nanoparticles, the tensile strength, compressive strength, and hardness increased from 328 to 385 MPa, 145 to 178 Mpa, and 302 to 724 VHN, respectively.