A process to manufacture porous oxide matrix/polycrystalline oxide fiber composites was developed and evaluated. The method uses infiltration of fiber cloths with an aqueous slurry of mullite/alumina powders to make prepregs. By careful manipulation of the interparticle pair potential in the slurry, a consolidated slurry with a high particle density is produced with a sufficiently low viscosity to allow efficient infiltration of the fiber tows. Vibration‐assisted infiltration of stacked, cloth prepregs in combination with a simple vacuum bag technique produced composites with homogeneous microstructures. The method has the additional advantage of allowing complex shapes to be made. Subsequent infiltration of the powder mixture with an alumina precursor was made to strengthen the matrix. The porous matrix, without fibers, possessed good thermal stability and showed linear shrinkage of 0.9% on heat treatment at 1200°C. Mechanical properties were evaluated in flexural testing in a manner that precluded interlaminar shear failure before failure via the tensile stresses. It was shown that the composite produced by this method was comparable to porous oxide matrix composites manufactured by other processes using the same fibers (N610 and N720). The ratio of notch strength to unnotch strength for a crack to width ratio of 0.5 was 0.7–0.9, indicating moderate notch sensitivity. Interlaminar shear strength, which is dominated by matrix strength, changed from 7 to 12 MPa for matrix porosity ranging from 38% to 43%, respectively. The porous microstructure did not change after aging at 1200°C for 100 h. Heat treatment at 1300°C for 100 h reduced the strength for the N610 and N720 composites by 35% and 20%, respectively, and increased their brittle nature.

No abstract

No abstract

No abstract

No abstract