Nickel supported on SiO2, SiO2–Al2O3, and Al2O3 catalysts have been prepared and studied for the reduction of benzene in reformate gasoline. The sol–gel method was used to prepare the catalysts. The evaluations were performed in a continuous fixed bed micro reactor fed by a flow of reformate gasoline at 398–473 K under atmospheric pressure. The physicochemical properties of the catalysts were obtained by XRD, FESEM, EDS-map, H2–adsorption, and N2 adsorption/desorption analysis to correlate the catalytic performances. To evaluate the performance of catalysts, different H2/benzene molar ratios and space velocities were used. The Ni/SiO2-b, Ni/SiO2-c, and Ni/FDU12 catalysts decreased the benzene content to less than 1 vol % at 423 K. The high toluene conversion by Ni/MSA and Ni/Mil-53­(Al) catalysts in comparison to other catalysts indicates that toluene hydrogenation is favored on these catalysts. The highest conversion of benzene in competitive hydrogenation was achieved at 423 K by the Ni/SiO2-c catalyst. In low H2/benzene molar ratio and space velocity conditions, benzene molecules find a greater chance of hydrogenation. Due to selective hydrogenation by Ni/SiO2-c, the RON is slightly reduced.

No abstract

No abstract

A series of platinum/zirconium–hexagonal mesoporous silica (Pt/Zr-HMS) catalysts with different molar ratios of Si/Zr have been prepared and used for reforming reaction. The prepared catalysts were characterized by XRD, XRF, NH3-TPD, FTIR, Py-IR, nitrogen sorption, SEM, and TGA (for studying the coke deposition) techniques. The effects of various amounts of zirconium on the activity, selectivity, and coke deposition in the temperature range of 200–500 °C were compared. By increasing the incorporation of Zr into the Pt-HMS structure, the acidity of catalysts increased. The results show that the catalytic activity and selectivity for desired products (especially isomerization products) increased with decreasing Si/Zr amount (or increasing zirconium content). The best i-C7 selectivity (64.1%) was observed for Zr(5)-HMS at T = 200 °C.

No abstract

No abstract