Tungsten (W) is a candidate material for Plasma facing materials of fusion reactors. During fusion reactor operation, not only irradiation damages but also transmutation elements such as rhenium (Re) and osmium (Os) are produced by neutron irradiation. As a result, the original pure tungsten changes to W-Re or W-Re-Os alloys. Thus, the mechanical and physical properties are expected to change. The aim of this study is to investigate the effects of transmutation elements on neutron irradiation hardening and microstructure changes of tungsten.To simulate the effects of transmutation elements, tungsten base model alloys were used in this study. The examined compositions of the alloys were selected from the calculated changes in solid solution area of W-Re-Os alloy. Neutron irradiation was performed in fast test reactor JOYO in JAEA. The irradiation damages and temperature ranges were 0.17-1.54 dpa and 400-750 C respectively. After the irradiation, Vickers hardness test and TEM observation were performed.There were clear differences between Re and Os in effects on irradiation hardening. In the case of W-Re alloys, when damages were less than 0.40 dpa, the irradiation hardenings were nearly equal to those of pure tungsten independent of Re addition. But when the damage was 1.54 dpa, the irradiation hardenings increased lineally with Re content. Microstructural observations showed that precipitations mainly formed in W-Re alloys. In the case of W-Os alloys, the irradiation hardenings (ÁHv) of W-3Os alloys were larger than those of pure tungsten. And the differences were about 400 independent of dpa and irradiation temperature. Effects of Re and Os on irradiation hardening based on the microstructural observations were discussed.

No abstract

Tungsten-based model alloys were fabricated to simulate compositional changes by neutron irradiation, performed in the JOYO fast test reactor. The irradiation damage range was 0.17-1.54 dpa and irradiation temperatures were 400, 500 and 750 C. After irradiation, microstructural observations and electrical resistivity measurements were carried out. A number of precipitates were observed after 1.54 dpa irradiation. Rhenium and osmium were precipitated by irradiation, which suppressed the formation of dislocation loops and voids. Structures induced by irradiation were not observed so much after 0.17 dpa irradiation. Electrical resistivity measurements showed that the effects of osmium on the electrical resistivity, related to impurity solution content, were larger than that of rhenium. Measurements of electrical resistivity of ternary alloys showed that the precipitation behavior was similar to that in binary alloys.