High-porosity nanostructured amorphous tungsten OXIDE (a-WO3) films were synthesized by a Hot Filament Chemical Vapor Deposition technique (HFCVD) and then transformed into a crystalline WO3 by simple thermal annealing. The a-WO3 films were annealed at 100, 300, and 500 °C for 10 min in an air environment. The films were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), micro-Raman spectroscopy, high-resolution transmission electron microscopy (HR-TEM), and UV–vis spectroscopy. Results revealed that the a-WO3 films were highly porous, composed of cauliflower-like structures made of nanoparticles with average sizes of 12 nm. It was shown that the effect of annealing on the morphology of the a-WO3 films leads to a sintering process. However, the morphology is conserved. It was found that at annealing temperatures of 100 °C, the a-WO3 films are of an amorphous nature, while at 300 °C, the films crystallize in the monoclinic phase of WO3. The calculated bandgap for the a-WO3 was 3.09 eV, and 2.53 eV for the film annealed at 500 °C. Finally, the results show that porous WO3 films preserve the morphology and maintain the porosity, even after the annealing at 500 °C.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.