Cubic GaN/GaAs (001) heterostructures were grown by RF-plasma assisted molecular beam epitaxy with different GaN nucleation temperatures. The heterostructures were studied by an open cell configuration of a photoacoustic experiment to obtain the effective thermal diffusivity (α) of the composite, which presented values varying from 14 to 28mm2/s. Also, a two-layer model was used in order to obtain the interfacial thermal conductivity (η), revealing values from 5 to 35W/cm2 K. Both α and η presented higher values for cubic GaN films grown with higher nucleation temperatures. The crystalline quality of the samples, studied with high resolution x-ray diffraction and photoluminescence measurements, showed that the increase in the nucleation temperature produced films with fewer defects, implying a dependence between the interfacial thermal properties and the bulk crystalline quality. This variation of η can be associated with phonon scattering due to disorder at the interface region. The results provide an important understanding of how the growth temperature of the nucleation layer can affect the quality and the properties of the cubic GaN.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.