The microstructure and mechanical strength of shock-deformed 70/30 copper-zinc alloy have been investigated by electron microscopy and hardness testing. Essentially three types of defect structures were produced in the alloy when subjected to shock compressive waves in a pressure range of 50-400 kb. These included dislocations, stacking faults and twin-type structures. The dislocation structures consist of bundles of parallel dislocations plus a limited number of stacking faults which have been activated on {111} planes. The absence of a dislocation cell structure appears to be a consequence of the low stacking fault energy of 70/30 copper-zinc alloy. At high pressures imperfect fault bands occur in the matrix which have a predominant twin orientation. The observed increase in residual hardness is attributable to the shock-induced dislocation and twin-fault densities. The magnitudes of such increases in strength were found to be consistent with recent theory of flow stress and work hardening.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.