Aminated poly(propylene) was prepared by reacting aliphatic primary diamines with maleic‐anhydride‐functionalized poly(propylene) by in situ melt reaction. Around 60–70% of the initial acid groups had reacted to form amide and imide groups as confirmed by the almost complete disappearance of the maleic anhydride peak in FT‐IR spectra. The molecular weight of the diamines had an influence on changes in molecular structure of the PP‐g‐NH2 as a result of secondary reactions such as chain extension and cross‐linking. PP‐g‐NH2 and polycarbonate were pressed into two‐layer films and their adhesion strength was measured. The results showed that PP‐g‐NH2 was a very effective adhesion promoter.

No abstract

SYNOPSISThe accelerated UV photodegradation process of low-density polyethylene films, formulated with two photostabilizers and two antioxidants, was studied to evaluate the effect of different combinations of UV stabilizers and antioxidants on the overall photodegradation process. An experimental design, consisting of 33 formulations with different additive ratios and a blank, was used to evaluate the performance of the four mixed additives. From each formulation, 200 micron-thick films were produced by the extrusion-blowing process. Samples from these films were submitted to accelerated UV aging, and the polymer degradation was measured by carbonyl group evolution, molecular weight distribution changes, and maximum elongation loss. The effect of the additive combination on the different degradation reactions is discussed qualitatively by using "relative variables" and a triangular diagram. 0 1996

The accelerated aging of six formulations of polypropylene highly loaded with calcium carbonate and containing a surfactant additive (stearic acid) as well as an ultraviolet (UV) stabilizer was studied. Degradation was followed by measuring mechanical properties (elongation percentage and impact resistance), the dynamic mechanical behavior and some chemical changes such as molecular weight and carbonyl group formation along with oxidation temperatures, found by chemiluminescence. The addition of 30 phr of filler to the polymer reduced the stability of the mixture, and the stearic acid used to treat the filler enhanced this effect considerably. On the other hand, the addition of the photostabilizer controlled to some extent such negative effects. though not completely. The most stable formulation was the polypropylene containing only the LJV stabilizer.

No abstract