Purpose
With recent advances in additive manufacturing (AM), polymer-based three-dimensional (3D) printers are available for relatively low cost and have found their way even in domestic and educational uses. However, the optimum conditions for processing and post-processing of different materials are yet to be determined. The purpose of this paper is to examine the effects of printing temperature, pattern and annealing conditions on tensile strength and modulus of samples printed with polylactic acid (PLA).
Design/methodology/approach
This study focuses on fused deposition modelling according to ISO/ASTM 52900 material extrusion AM. To print parts with maximum mechanical properties, the printing variables must be optimised. To determine the printing and annealing condition on physical and mechanical properties of PLA-based parts, dogbone-shaped tensile samples were printed at four different nozzle temperatures and five different filling patterns embedded in a 3D printing software. The samples were further annealed at three different temperatures for three different time intervals. The mechanical properties were evaluated and the changes in mechanical properties were analysed with the help of rheometrical measurements.
Findings
The results showed that printing condition has a significant influence on final properties, for example, the strain at break value increases with increasing nozzle temperature from 34 to 56 MPa, which is close to the value of the injected sample, namely, 65 MPa. While tensile strength increases with printing temperature, the annealing process has negative effects on the mechanical properties of samples.
Originality/value
The authors observed that traditional findings in polymer science, for example, the relationship between processing and annealing temperature, must be re-evaluated when applied in 3D printing because of major differences in processing conditions resulting from the layer-by-layer manufacturing.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.