Abstract. Sodium alginate obtained from the extraction of brown algae is used as the backbone for the synthesis of superabsorbent nanocomposite copolymerization. The first stage of extraction is the demineralization process using 0.1 M HCl solution and then 2% Na2CO3 solution for 2 hours at 60°C. The rendement of sodium alginate obtained was 44.32% with molecular weight of 40680 g/mol with measurement of the intrinsic viscosity. FTIR spectra of sodium alginate showed mannuronic acid functional group at wavenumber 884 cm -1 and the uronic acid at wavenumber 939 cm -1 , OH functional group at wavenumber 3200-3400 cm -1 , and CH2 stretching at wavenumber 2928 cm -1 . The diffraction pattern of isolated sodium alginate has specific 2θ at 13.068 and 21.096, amorphous intensity found specific 2θ at 18.058, and the obtained crystallinity degree of the sodium alginate is equal to 29.292% from the XRD analysis. The morphological analysis by SEM shows fibrils of isolated sodium alginate. The success isolation of sodium alginate from brown algae is supported by DSC which shows the decomposition temperature of pure sodium alginate and isolated alginate have close values, namely 251.12°C for pure sodium alginate and 229.90°C for isolated sodium alginate.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.