The resource utilization of phosphogypsum is confronted with great challenge. Of all the different methods for phosphogypsum resource utilization, using phosphocypsum to fabricate calcium fluoride (CaF2) is an effective resource utilization method. In this work, high-quality nano-calcium fluoride was successfully prepared in aqueous solution using calcined phosphogypsum by direct precipitation method. A series of orthogonal experiments were carried out in study. Here, the calcined phosphogypsum powder was mixed with NH4F to react at 40°C for 70 min according to the optimum molar ratio (Ca/ F=0.4). Meanwhile, the residue obtained by separating the mixture reacted was dried at 120°C for 90min. After preparation, the nano-calcium fluoride was analyzed by X-ray diffraction and scanning electron microscope, results found that the average particle diameter of calcium fluoride was around 70 nm. This work could increase the industrial chain of phosphogypsum application and apply a method to solve the fluorite resource shortage.

A precipitation reaction method was employed to prepare mesopore calcium carbonate (CaCO3) using rape flower pollen as the template. CaCO3 adsorbent was characterized using X-ray diffraction (XRD), scanning electronic microscopy (SEM), and Brunner−Emmet−Teller measurements (BET). The equilibrium adsorption data on amoxicillin were explained using Langmuir, Freundlich, and Temkin adsorption isotherm models. The pseudo-first order, second order, pseudo-second order, and intra-particle diffusion kinetic models were used to explore adsorption kinetics. Equilibrium adsorption of as-prepared CaCO3 was better depicted using the Langmuir adsorption model with an R2 of 0.9948. The separation factor (RL) was found to be in the range of 0 < RL < 1, indicating the favorable adsorption of amoxicillin. The adsorption capacity of mesopore CaCO3 reached 13.49 mg·g−1 in 0.2 g∙L−1 amoxicillin solution. The values of adsorption thermodynamic parameters (ΔHθ, ΔSθ, ΔGθ) were obtained. In addition, the adsorption process turned out to be endothermic and spontaneous for the CaCO3 product at 298 K, 308 K, and 318 K.

The electro-photocatalytic degradation of amoxicillin in aqueous solution was investigated using single factor test by the potassium permanganate method for measuring the values of chemical oxygen demand (CODMn). Batch experiments were carried out successfully under different conditions, including initial amoxicillin concentration, calcium titanate dosage, pH, UV irradiation time, electrolyte and temperature. The experimental results show that there is a great difference between electro-photocatalytic and photocatalitic degradation. The maximum electro-photocatalytic degradation efficiency can increase to 79% under the experimental conditions of 200 mL amoxicillin solution (100 mg L-1) with 0.5 g calcium titanate by pH=3 for 120 min irradiation and 0.058 g sodium chloride as electrolyte at 318.5K. In addition, the reaction rate constant of 0.00848~0.01349 min-1, activation energy of 9.8934 kJ mol-1 and the pre-exponential factor of 0.5728 were obtained based on kinetics studies, indicating that the electro-photocatalytic reaction approximately followed the first-order kinetics model.