A new powder production method has been developed to speed up the search for novel alloys for additive manufacturing. The technique involves an ultrasonically agitated cold crucible installed at the top of a 20 kHz ultrasonic sonotrode. The material is melted with an electric arc and undergoes pulverization with standing wave vibrations. Several different alloys in various forms, including noble and metallic glass alloys, were chosen to test the process. The atomized particles showed exceptional sphericity, while powder output suitable for additive manufacturing reached up to 60%. The AMZ4 metallic glass powder remained amorphous below the 50 μm fraction, while tungsten addition led to crystallization in each fraction. Minor contamination and high Mn and Zn evaporation, especially in the finest particles, was observed in atomized powders. The innovative ultrasonic atomization method appears as a promising tool for material scientists to develop powders with tailored chemical composition, size and structure.
Selective Laser Melting (SLM) is a manufacturing technique that is currently used for the production of functional parts that are difficult to form by the traditional methods such as casting or CNC (Computer Numerical Control) cutting from a wide range of metallic materials. In our study, a mixture of commercially pure titanium (Ti) and 15% at. aluminum nitride (AlN) was Selective Laser Melted to form three-dimensional objects. The obtained 4 mm edge cubes with an energy density that varied from 70 to 140 J/mm3 were examined in terms of their microstructure, chemical and phase composition, porosity, and Vickers microhardness. Scanning Electron Microscopy (SEM) observations of the etched samples showed inhomogeneities in the form of pores and unmelted and partly melted AlN particles in the fine-grained dendritic matrix, which is typical for titanium nitrides and titanium aluminum nitrides. The AlN particles remained unmelted in samples, but no porosity was observed in the interface area between them and the dendritic matrix. Additionally, samples fabricated with the presintering step had zones with different sizes of dendrites, suggesting a differing chemical composition of the matrix and the possibility of the formation of the phases forming an Ti–Al–N ternary system. The chemical composition in the microareas of the samples was determined using Energy Dispersive X-Ray Spectroscopy (EDS) and revealed differences in the homogeneity of the samples depending on the SLM process parameters and the additional presintering step. The phase composition, examined using X-ray Diffraction analysis (XRD), showed that samples were formed from Ti, TiN, and AlN phases. Porosity tests carried out using a computer microtomography revealed porosities in a range from 7% to 17.5%. The formed material was characterized by a relatively high hardness exceeding 700 HV0.2 over the entire cross-section, which depended on the manufacturing conditions.
Finishing operations are one of the most challenging tasks during a manufacturing process, and are responsible for achieving dimensional accuracy of the manufactured parts and the desired surface topography properties. One of the most advanced finishing technologies is grinding. However, typical grinding processes have limitations in the acquired surface topography properties, especially in finishing difficult to cut materials such as Inconel 625. To overcome this limitation, a new type of grinding wheel is proposed. The tool is made up of grains of different sizes, which results in less damage to the work surface and an enhancement in the manufacturing process. In this article, the results of an experimental study of the surface grinding process of Inconel 625 with single-granular and multi-granular wheels are presented. The influence of various input parameters on the roughness parameter (Sa) and surface topography was investigated. Statistical models of the grinding process were developed based on our research. Studies showed that with an increase in the cutting speed, the surface roughness values of the machined samples decreased (Sa = 0.9 μm for a Vc of 33 m/s for a multigranular wheel). Observation of the grinding process showed an unfavorable effect of a low grinding wheel speed on the machined surface. For both conventional and multigranular wheels, the highest value for the Sa parameter was obtained for Vc = 13 m/s. Regarding the surface topography, the observed surfaces did not show defects over large areas in the cases of both wheels. However, a smaller portion of single traces of active abrasive grains was observed in the case of the multi-granular wheel, indicating that this tool performs better finishing operations.
The GeniCore Upgraded Field Assisted Sintering Technology U-FAST was applied to the sintering of a commercial Zr-based bulk metallic glass powder AMZ4. The XRD, SEM and DSC analysis of the sintered compacts showed the benefit of the U-FAST method as an enabler for the production of fully amorphous samples with 100% relative density when sintering at 420 °C/480 s (693 K/480 s) and 440 °C/ 60 s (713 K/480 s). The hardness values for fully amorphous samples, over HV1 519, surpass cast materials and 1625 MPa compressive strengths are comparable to commercial cast products. The advantage of the U-FAST technology in this work is attributed to the high heating and cooling rates inherent to ultra-short pulses, which allow to maintain metastable structures and achieve better temperature control during the process. Increasing sintering temperature and time led to the crystallization of the materials. The geometry and material of the dies and punch determine the thermal inertia and pressure distribution inside the compacts, thus affecting the properties of the near net shape NNS compacts made using the U-FAST device.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.