synopsisThe cure behavior and thermal degradation of high Tg epoxy systems have been investigated by comparing their isothermal time-temperature-transformation (TIT) diagrams. The formulations were prepared from di-and trifunctional epoxy resins, and their mixtures, with stoichiometric amounts of a tetrafunctional aromatic diamine. The maximum glass transition temperatures (TgJ were 229°C and > 324°C for the fully cured di-and trifunctional epoxy materials, respectively. Increasing functionality of the reactants decreases the times to gelation and to vitrification, and increases the difference between Tg after prolonged isothermal cure and the temperature of cure. At high temperatures, there is competition between cure and thermal degradation. The latter was characterized by two main processes which involved devitrification (decrease of modulus and T,) and revitrification (char formation). The experimentally inaccessible Tcm (352T) for the trifunctional epoxy material was obtained by extrapolation from the values of Tgm of the less highly crosslinked systems using a relationship between the glass transition temperature, crosslink density, and chemical structure.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.