The effect of overheating of the melt and cooling rate of alloys of the Al-Cu system with a copper content of 25.0 – 36.0% ( mass.), the rest of the aluminum is investigated. It is shown that an overheating of the liquid at 50 – 100 K above the liquid-liquid line leads to the formation of a fine-dispersed eutectic structure and the inhibition of the formation of primary aluminum crystals in the pre-evacuation of alloys and the Al2Cu phase in hypereuvtectic alloys, in accordance. An increase in the melt overheating temperature by 150 K above the liquid-liquid line and the subsequent cooling at 103 – 104 K/s leads to the complete inhibition of the formation of primary crystals. An overheating of the melt on 100 – 150 K alloys above the liquid line and subsequent cooling with a velocity of 103 – 104 K /s reduces the rate of corrosion by 30 – 45% and increases the numerical value in 1.3 – 1.45 times the relative wear resistance, and the brittleness of alloys decreases in 1.2 – 1.35 times in comparison with the samples after casting.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.