The aim of this study was to evaluate of pre-heating, filler contents and ceramic thickness on film thickness, microshear bond strength, degree of conversion and color change on ceramic veneers. Two experimental composites were prepared (Bis-GMA/UDMA/BisEMA/ TEGDMA), with different amounts of filler (65% or 50%wt) simulating a conventional and a flowable composite. The flowable (F) was used at room temperature and, the conventional either at room temperature (C) or pre-heated (CPH). Disk-shaped ceramics with different thickness (0.4 mm, 0.8 mm, 1.5 mm) were prepared. The film thickness was evaluated according to the ISO 4049 (n=10). The microshear bond strength (n=10) was evaluated in enamel using tubing specimens light-cured through the ceramic veneer. The degree of conversion was evaluated using Raman spectroscopy. The color change of the ceramic restorations (n=10) was evaluated by spectrophotometry. The results were submitted to 2-way ANOVA and Tukey’s post hoc test (a=5%). For the film thickness 1-way ANOVA was used (a=5%). The C presented the thicker film thickness; the CPH produced a similar film thickness in comparison to the F. All composites showed similar microshear bond strength. The degree of conversion of the F was higher than the C and CPH. The degree of conversion of the composites photo-activated through a 0.4 mm was higher than the composites photo-activated through thicker ceramics. The C showed the highest color change, while the CPH showed similar color change to the F. In conclusion, pre-heated conventional composites seem to be a potential alternative to lute ceramic veneers such as the flowable composites.
This study aimed to assess the dimensional accuracy of five commercial alginates verified in stone casts. Methods: Each alginate impression (Cavex ColorChange, Cavex Holland BV; Jeltrate Plus, Dentsply; Hydrogum, Zhermack; Kromopan 100, Lascod; Ezact Kromm, Vigodent) was performed on partially edentulous standard stainless steel mandibular arch cast with reference points on teeth 33, 43, 37 and 47. On the stainless steel cast, the anteroposterior (33-37 and 43-47) and transverse (33-43 and 37-47) distances were measured in a stereomicroscope at 30x magnification and 0.5 μm accuracy. The distances between these points were measured three times, obtaining an average, which was analyzed statistically and compared with the distances obtained from the stone casts. For each alginate the casts were poured gypsum (n = 5) immediately and after a period of 1, 2, 3 and 5 days of the impression procedure. Results: The dimensional accuracy values of stone and stainless steel casts were analyzed statistically by two-way ANOVA and Tukey's test (α=0.05). The results showed significant differences between the alginates; however, no differences in dimensional accuracy were found among the different storage times of alginate impression. Conclusions: It can be concluded that the alginate impressions can be stored for up to 5 days.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.