To further promote the research and application of resin type waterproof adhesive layer materials, the types, relevant specifications, and research trends of resin type waterproof adhesive layer in China are comprehensively investigated. The performance evaluation indicators, performance requirement, and requirements in different specifications are systematically analyzed, and the key performance evaluation indicators are recommended. The basic properties of common resin type waterproof adhesive layer materials are studied, and the bonding properties of different resin waterproof adhesive layers were compared and evaluated. The results showed that pull-out strength, shear strength, tensile strength, elongation at break, low temperature flexibility, and impermeability are the key performance evaluation indicators of resin waterproof adhesive layer. The tensile property, corrosion resistance, and water impermeability of resin type waterproof adhesive layer material are good, the flexibility of epoxy resin type waterproof adhesive layer material is poor, and the flexibility of methyl methacrylate (MMA) waterproof adhesive layer material is good. The bonding performance of the epoxy resin waterproof adhesive layer is better than that of the MMA. As the temperature rises, the bonding performance of the two waterproof adhesive layers is significantly reduced. At 60°C, the average pull-out strengths of the epoxy resin and MMA waterproof adhesive layer were 1.83 MPa and 1.47 MPa, respectively.
With the increase in traffic volume and axle load, the requirement of road quality is continuously improving, and high modulus asphalt has attracted the attention of researchers due to its excellent road service performance and economic benefits. In order to further improve the durability and use quality of Chinese roads, realize the scientific evaluation of the performance of high modulus asphalt and its mixture, and further promote the development of high modulus asphalt technology in China, the performance indexes of high modulus asphalt and its mixture in China were comprehensively investigated. The differences in high- and low-temperature performance of matrix asphalt, basic modified high modulus asphalt, and composite modified high modulus asphalt were compared and evaluated. Based on the results of mathematical statistics and the relevant specifications of high modulus asphalt in China, the performance grades of high modulus asphalt and its mixture were proposed. The results showed that compared with the basic asphalt, the softening points of the basic modified high modulus asphalt and the composite modified high modulus asphalt were increased by 18.76% and 82.89%, respectively, and the rutting factors were increased by 2 and 9 times, respectively, but the improvement effect of the low-temperature performance of the high modulus asphalt was not obvious. Based on the data statistics node and relevant Chinese regulations, high modulus asphalt and its mixtures were divided into four grades: excellent, good, fair, and poor, aiming to provide scientific suggestions for the wide application of high modulus asphalt.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.