We present x-ray absorption and emission experiments and ab initio calculations showing that the size of carbon diamond must be reduced to at least 2 nm, in order to observe an increase of its optical gap, at variance with Si and Ge where quantum confinement effects persist up to 6-7 nm. In addition, our calculations show that the surface of nanodiamond particles larger than approximately 1 nm reconstructs in a fullerenelike manner, giving rise to a new family of carbon clusters: bucky diamonds. Signatures of these surface reconstructions are compatible with pre-edge features observed in measured absorption spectra.

The exciton binding energy (EBE) in CdSe quantum dots (QDs) has been determined using X-ray spectroscopy. Using X-ray absorption and photoemission spectroscopy, the conduction band (CB) and valence band (VB) edge shifts as a function of particle size have been determined and combined to obtain the true band gap of the QDs (i.e., without an exciton). These values can be compared to the excitonic gap obtained using optical spectroscopy to determine the EBE. The experimental EBE results are compared with theoretical calculations on the EBE and show excellent agreement.

The IBM/TENN/TULANE/LLNL/LBL Beamline 8.0 at the advanced light source combining a 5.0 cm, 89 period undulator with a high-throughput, high-resolution spherical grating monochromator, provides a powerful excitation source over a spectral range of 70-1200 eV for surface physics and material science research. The beamline progress and the first experimental results obtained with a fluorescence end station on graphite and titanium oxides are presented here. The dispersive features in K emission spectra of graphite excited near threshold, and found a clear relationship between them and graphite band structure are observed. The monochromator is operated at a resolving power of roughly 2000, while the spectrometer has a resolving power of 400 for these fluorescence experiments. Q

Self-assembled monolayers (SAMs) consisting of alkanethiols and similar sulfurcontaining molecules on noble metal substrates are extensively used and explored for various chemical and biological surface-functionalization in the scientific community. SAMs consisting of thiol-or disulfide-containing molecules adsorbed on gold are commonly used due to their ease of preparation and stability. However, the gold-thiolate bond is easily and rapidly oxidized under ambient conditions, adversely affecting SAM quality and structure. Here, the oxidation of dodecanethiol on gold is explored for various 12-hour exposures to ambient laboratory air and light. SAM samples are freshly prepared, air-exposed, and stored in small, capped vials. X-ray photoelectron spectroscopy (XPS) reveals nearly complete oxidation of the thiolate in air-exposed samples, and a decrease in carbon signal on the surface. Near-edge X-ray absorption fine structure spectroscopy (NEXAFS) at the Carbon K-edge shows a loss of upright orientational order upon air-exposure. Alternatively,