A new hydrothermal route for preparing biphasic calcium phosphate monoliths is proposed. Firstly, a slurry of beta-tricalcium phosphate/ortho-phosphoric acid (b-TCP/H3PO4) is cast into the desired final shape and size to obtain a block composed of dicalcium phosphate dihydrate (DCPD) and b-TCP. This block is then treated in 1.0 M Na2HPO4 at 60 °C in order to hydrolyze the DCPD into Ca10-x(HPO4)x(PO4) 6-x(OH)2-x (CDHA) and Ca8H2(PO4)6 .5H2O (OCP). The result is a monolithic piece which preserves the initial shape and size, but which is composed instead of CDHA, OCP, and b-TCP. During the initial stage, when the pH is slightly alkaline, the product of DCPD hydrolysis is CDHA. However, when a neutral or slightly acidic pH is reached OCP is formed. Test samples processed by this method showed complete conversion of DCPD into CDHA and OCP after 112 h of hydrolysis, and with a compressive strength of 16.2 MPa, similar to cancellous bone
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.