The doping of biologically meaningful ions into biphasic calcium phosphate (BCP) bioceramics, which exhibit biocompatibility with human body parts, has led to their effective use in biomedical applications in recent years.
This work reports on a novel approach to deposit composite coatings based on biphasic calcium phosphate (BCP) incorporating graphene oxide (GO) on 316L stainless steel (316L SS) and on its protective nature against corrosion in the simulated body fluid (SBF). For this purpose, 2-dimensional GO was successfully incorporated in 1% and 3% weight ratios as mechanical strength enhancer and pore size reducer for the prepared coatings. It was observed that upon increasing the GO content, the corrosion rate was drastically decreased when compared to pristine BCP coating. The corrosion resistance polarization results are in good agreement with the test results obtained for SBF immersion study. The size of the particles has significantly decreased, as shown by transmission electron microscopy (from 190 to 27 nm). The experimental results indicate that the composite hydroxyapatite-β-tricalcium phosphate-GO (HAp-β-TCP-GO) coatings enhanced the corrosion resistance of the surgical grade 316L SS, turning it a better implanting option for orthopedic applications.
Mesoporous silica network nanotubes were fabricated using both organic and inorganic templates such as citric acid (CA), cetyltrimethylammonium bromide (CTAB), and sodium bicarbonate (SBC). The phase analysis of synthesized silica network was confirmed by X-ray diffractometer (XRD) analysis, and the present functional groups were revealed by Fourier Transformer Infrared Spectroscopy (FTIR) and the formation of tubular morphology was analyzed by Transmission Electron Microscopy (TEM). The mesoporous nature of each template sample was studied using Brunauer–Emmett–Teller (BET) instrument. The surface area and porous size were calculated successfully for fabricated silica network nanotubes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.