Silicon nitride (Si3N4) based ceramic tools exhibit good machinability in cutting materials such as gray cast iron, ductile iron, malleable cast iron, and superalloys due to excellent high-temperature mechanical properties. In this paper, high-performance Si3N4-based ceramic tools containing tungsten carbide (WC) and cobalt (Co) were studied. Effects of the WC content and Co content on mechanical properties and a microstructure of Si3N4-based ceramic materials were analyzed. Results showed that Si3N4-based ceramic material containing 10 wt % WC and 1 wt % Co had the best comprehensive mechanical properties at a sintering temperature of 1650 °C and holding time of 6 min, achieving Vickers hardness, fracture toughness, and room temperature bending strength of 16.96 GPa, 7.26 MPa·m1/2, and 1132 MPa, respectively. The microstructure of Si3N4-based ceramic tool material is uniform without obvious abnormal growth. The Si3N4-based ceramic tool was mainly composed of α-Si3N4, β-Si3N4, and WC phases.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.